Parabeam Industrie Paraglass 18 3D Glass Fabric

Category Ceramic , Glass , Glass Fiber , Other Engineering Material , Composite Core Material , Composite Fibers
Manufacturer Parabeam Industrie
Trade Name Paraglass
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Parabeam Industrie Paraglass 18 3D Glass Fabric.pdf
  Online Service   lookpolymers   27660005
Material Notes:
Parabeam® 3D Glass Fabric is a fabric woven out of a 100% E-glass yarn and consists of two decklayers bonded together by vertical piles in a sandwich structure. These piles are woven into the decklayers thus forming an integral sandwich structure.When the Parabeam® is impregnated with a thermoset resin, the fabric absorbs the resin and due to the capillary forces of the piles, the fabric rises to the preset height.In this one-step process a lightweight and strong sandwich laminate is formed that offers excellent mechanical properties. Parabeam® can be used for many applications in the composite industry while offering multiple advantages against traditional sandwiches and solid laminates such as woods, foams, balsa, honeycombs and more. Information provided by the manufacturer, Parabeam Industrie, The Netherlands.
Mechanical Properties Metric English Comments
Compressive Yield Strength >= 0.700 MPa
>= 102 psi
0.900 MPa
131 psi
Typical; ASTM C365
Shear Modulus >= 0.000800 GPa
>= 0.116 ksi
0.00180 GPa
0.261 ksi
Typical; ASTM C273
Shear Strength >= 0.100 MPa
>= 14.5 psi
0.100 MPa
14.5 psi
Typical; ASTM C273
Thermal Properties Metric English Comments
Thermal Conductivity 0.0800 W/m-K
0.555 BTU-in/hr-ft²-°F
DIN 52616