Parker Chomerics CHO-SEAL 1310 Conductive Elastomer

Category	Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone
Manufacturer	Parker Chomerics
Trade Name	CHO-SEAL
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Parker Chomerics CHO-SEAL 1310 Conductive Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Moderate performance in non-corrosive environments, no corrosion or fluid resistance; material of choice for small, delicate injection-molded parts or large dimension extrusionsMolded onlyRoHS CompliantInformation provided by Chomerics

Physical Properties	Metric	English	Comments
Specific Gravity	1.55 - 2.05 g/cc	1.55 - 2.05 g/cc	ASTM D792
Deformation	0.0060 %	0.0060 %	.75 pli; Predicted by FEA
	0.010 %	0.010 %	1.25 pli; Predicted by FEA
	0.014 %	0.014 %	2 pli; Predicted by FEA
	0.018 %	0.018 %	2.9 pli; Predicted by FEA

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	60 - 80	60 - 80	ASTM D2240
Tensile Strength at Break	>= 1.38 MPa	>= 200 psi	ASTM D412
Elongation at Break	>= 100 %	>= 100 %	ASTM D412
Compression Set	<= 35 % @Temperature 100 °C, Time 252000 sec	<= 35 % @Temperature 212 °F, Time 70.0 hour	ASTM D395 Method B

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	160 °C	320 °F
Minimum Service Temperature, Air	-40.0 °C	-40.0 °F	Flex TR10; ASTM D1329
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Volume Resistivity	0.010 ohm-cm	0.010 ohm-cm	without psa; CEPS-0002
Shielding Effectiveness	>= 80 dB @Frequency 1.00e+10 Hz	>= 80 dB @Frequency 1.00e+10 Hz	Plane Wave; CHO-TM-TP08
	>= 90 dB @Frequency 2.00e+9 Hz	>= 90 dB @Frequency 2.00e+9 Hz	Plane Wave; CHO-TM-TP08
	>= 100 dB @Frequency 1.00e+8 Hz	>= 100 dB @Frequency 1.00e+8 Hz	E Field; CHO-TM-TP08
	>= 100 dB @Frequency 5.00e+8 Hz	>= 100 dB @Frequency 5.00e+8 Hz	E Field; CHO-TM-TP08

Descriptive Properties	Value	Comments
Binder	Silicone
Filler	Ag/Glass
Heat Aging	<0.01ohm-cm	CEPS-0002