PolyOne Geon™ HTX Ultra LA427Plus Polyvinyl Chloride Alloy (PVC Alloy)
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ HTX Ultra LA427Plus Polyvinyl Chloride Alloy (PVC Alloy).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties based on Geon HTX Ultra LA427Plus Natural 0000Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 79 | 79 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.99 GPa | 434 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 80.7 MPa | 11700 psi | ASTM D790 |
| Flexural Modulus | 2.94 GPa | 426 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded; ASTM D256A |
| Dart Drop Total Energy | 13.3 J/cm @Temperature 23.0 °C |
0.0249 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 26.7 J/cm @Temperature 23.0 °C |
0.0500 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 64.0 µm/m-°C | 35.6 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.9 °C @Thickness 3.18 mm |
201 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| 95.0 °C @Thickness 3.18 mm |
203 °F @Thickness 0.125 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.1 °C @Thickness 3.18 mm |
187 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| 88.9 °C @Thickness 3.18 mm |
192 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 174 - 193 °C | 345 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ease of Sizing | Acceptable | |
| Features | High Stiffness | |
| Low CLTE | ||
| Forms | Pellets | |
| Generic Material | PVC Alloy | |
| Generic Name | Polyvinyl Chloride Alloy (PVC Alloy) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 13355 | ASTM D1784 |
| 4-20034-30-000 | ASTM D4216 | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Profiles |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 FRC 3 PA6, flame retardant
- SABIC Innovative Plastics Cycolac® EX58 ABS (Europe-Africa-Middle East)
- Polykemi AB POLYfill PPH GF4030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- Kingfa FRHIPS-960 Flame Retardant Polystyrene
- Monmouth Rubber & Plastics Durafoamâ„¢ P392SHD EPDM
- Shin-Etsu Silicones X-22-6711B Fluid
- Arkema Group Orgalloy® LE 60ES03 Flexible Nylon Alloy (Conditioned)
- ATI Allvac® Vasco® 316-L Specialty Steel, Heat Treatment: 1038°C (1900°F) Anneal
- 3M 9039 Double Coated Tapes with Adhesive 300
Copyright © lookpolymers.com All Rights Reserved