Samsung Cheil Industries Starex® SF-301H Expandable Polystyrene (EPS) FR
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Expanded Polystyrene (EPS) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SF-301H Expandable Polystyrene (EPS) FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: High Strength, High ExpansionTypical Application : InsulationInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 - 1.05 g/cc | 1.03 - 1.05 g/cc | |
| Density | 0.0149 g/cc | 0.000538 lb/in³ | Based on 70 times expansion |
| Bead Size | 0.720 - 0.960 mm | 0.0283 - 0.0378 in | JIS Z8801 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 3.00 MPa | 435 psi | @ 20 kg/m<sup>2</sup>; ASTM DC201 |
| Compressive Strength | >= 1.30 MPa | >= 189 psi | @ 20 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
| Chemical Properties | Metric | English | Comments |
|---|---|---|---|
| Blowing Agent Content | 6.0 - 7.0 % | 6.0 - 7.0 % | Pentane |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Blocking | <1% | |
| Expandability | 70 Times | Expansion for 5 min Cheil Method |
| Fusion | >65% | Cheil Method |
| Polymer Content | 93-94% |
Users viewing this material also viewed the following:
- Mytex Polymers AS78L(W)-GM-02 Polypropylene, Rubber modified, Compounded
- Kraton® D1160 E (SIS) Linear Triblock Copolymer
- Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled
- Styron INSPIREâ„¢ DLGF 9621.00 Compounded Polypropylene, 60% LGF
- DuPont™ Kapton® 150FN019 Polyimide/FEP Composite Film
- DuPont Performance Polymers Zytel® 70G35HSRX BK099 Nylon 66 (Unverified Data**)
- Braskem S1522 LDPE Blow Molding Polyethylene
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 78A
- Latrobe LSS™ 440C Stainless Steel Knife (ASTM A276)
- Guarniflon PTFE G403 Polytetrafluoroethylene 15% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved