Sharadaa Ceramics REFCAST LC45 Low Cement Castables
| Category | Ceramic |
| Manufacturer | Sharadaa Ceramics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sharadaa Ceramics REFCAST LC45 Low Cement Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: We bring to our clients a range of Low Cement Castables, that are available in varied alumina content and service range. Designed for abrasion resistance application, these are widely used in furnaces such as ladle back up lining, sintering furnace roof and soaking pit covers.Information provided by Sharadaa Ceramics Pvt. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | >= 2.30 g/cc | >= 0.0831 lb/in³ | Dried at 110°C |
| Grain Size | <= 6000 µm | <= 6000 µm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.00981 GPa @Temperature 110 °C |
1.42 ksi @Temperature 230 °F |
|
| 0.0123 GPa @Temperature 1100 °C |
1.78 ksi @Temperature 2010 °F |
||
| 0.0162 GPa @Temperature 1500 °C |
2.35 ksi @Temperature 2730 °F |
||
| Compressive Strength | 73.5 MPa @Temperature 110 °C |
10700 psi @Temperature 230 °F |
Cold Crushing |
| 93.2 MPa @Temperature 1100 °C |
13500 psi @Temperature 2010 °F |
Cold Crushing | |
| 108 MPa @Temperature 1500 °C |
15600 psi @Temperature 2730 °F |
Cold Crushing | |
| 19.6 MPa @Time 86400 sec |
2840 psi @Time 24.0 hour |
Cold Crushing |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.976 W/m-K @Temperature 400 °C, Time 10800 sec |
6.77 BTU-in/hr-ft²-°F @Temperature 752 °F, Time 3.00 hour |
|
| 1.22 W/m-K @Temperature 600 °C, Time 10800 sec |
8.47 BTU-in/hr-ft²-°F @Temperature 1110 °F, Time 3.00 hour |
||
| 1.35 W/m-K @Temperature 800 °C, Time 10800 sec |
9.37 BTU-in/hr-ft²-°F @Temperature 1470 °F, Time 3.00 hour |
||
| Maximum Service Temperature, Air | 1550 °C | 2820 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | >= 45 % | >= 45 % | |
| Fe2O3 | <= 1.5 % | <= 1.5 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Permanent Linear Change | -0.2 - 0.2% | 800°C |
| -0.3 - 0.3% | 1100°C | |
| -1.0 -1.0% | 1500°C | |
| Refractoriness | >1717°C | |
| Thermal Expansion | 0.5 | 1000°C, Reversible |
| Water Required to Mix | 4 - 5% |
Users viewing this material also viewed the following:
- Polyplastic Armoflen® PO MF 65-2 Linear Low Density Polyethylene, 65% Calcium Carbonate
- RheTech Products HP514-00 14% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural
- Gouda Vuurvast CURON 150 H Dense Refractory Castable
- Seals Eastern 7040 Fluorocarbon-Elastomer
- Teknor Apex Uniprene® 73A Polyvinyl Chloride, Flexible
- Master Bond MB600SCN Aqueous Based Electrically Conductive Sodium Silicate Coating
- Total 50100.1 HDPE blow molding
- Toho Tenax Besfight® G60-600 12K UMA-5C A303 Continuous Filament Carbon Fiber
- American Computer Optics High Transmission Filter 6 mm
- SABIC Innovative Plastics NORYL 115 PPE+HIPS (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved