Zyvex Performance Materials Epovex™ Nano-Engineered Composite Epoxy Adhesive Liquid

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive, Flexible
Manufacturer Zyvex Performance Materials (ZPM)
Trade Name Epovex™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zyvex Performance Materials Epovex™ Nano-Engineered Composite Epoxy Adhesive Liquid.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Epovex® Adhesive is a carbon nanotube enhanced ambient or elevated temperature cure two-part epoxy adhesive. Used for bonding, laminating, filling or potting, Epovex is ideal for many metals, woods, masonry products and some plastics and rubbers. Epovex was also designed to bond Zyvex Technologies’ Arovex® composites. Additional fillers or glass micro-beads may be added to control sag qualities or to control bond-line thickness to a specific thickness or specification.Features: Excellent flexibilityVery high T-peel strengthsVery high tensile shear strengths.
Mechanical Properties Metric English Comments
Shear Strength 15.9 MPa

@Temperature 60.0 °C
 2300 psi

@Temperature 140 °F
 Cure cycle: 7 days @ RT, with Aced Etched 6061-T6 Aluminum
19.9 MPa

@Temperature 23.9 °C
 2880 psi

@Temperature 75.0 °F
 Cure cycle: 7 days @ RT (+7 days ethyl alcohol soak), with Aced Etched 6061-T6 Aluminum
20.0 MPa

@Temperature 23.9 °C
 2900 psi

@Temperature 75.0 °F
 Cure cycle: 7 days @ RT (+7 days gasoline soak) , with Aced Etched 6061-T6 Aluminum
20.3 MPa

@Temperature 23.9 °C
 2940 psi

@Temperature 75.0 °F
 – 6061-T6 Aluminum (abraded), with Arovex Carbon Fiber Epoxy Laminate
22.1 MPa

@Temperature 23.9 °C
 3200 psi

@Temperature 75.0 °F
 Cure cycle: 3 days @ RT, with Aced Etched 6061-T6 Aluminum
23.7 MPa

@Temperature 23.9 °C
 3440 psi

@Temperature 75.0 °F
 Arovex (abraded), with Arovex Carbon Fiber Epoxy Laminate
24.0 MPa

@Temperature 23.9 °C
 3480 psi

@Temperature 75.0 °F
 Cure cycle: 7 days @ RT (+7 days water soak), with Aced Etched 6061-T6 Aluminum
24.1 MPa

@Temperature 23.9 °C
 3500 psi

@Temperature 75.0 °F
 Cure cycle: 5 days @ RT, with Aced Etched 6061-T6 Aluminum
24.4 MPa

@Temperature 23.9 °C
 3540 psi

@Temperature 75.0 °F
 Cure cycle: 7 days @ RT, with Aced Etched 6061-T6 Aluminum
25.4 MPa

@Temperature 23.9 °C
 3690 psi

@Temperature 75.0 °F
 (+7 days water soak), with Arovex Carbon Fiber Epoxy Laminate
27.6 MPa

@Temperature 23.9 °C
 4000 psi

@Temperature 75.0 °F
 Cure cycle: 12 hrs @ RT + 1 hr @ 176°F, with Aced Etched 6061-T6 Aluminum
30.3 MPa

@Temperature -40.0 °C
 4400 psi

@Temperature -40.0 °F
 Cure cycle: 7 days @ RT, with Aced Etched 6061-T6 Aluminum
31.1 MPa

@Temperature 23.9 °C
 4510 psi

@Temperature 75.0 °F
 Cure cycle: 2 hrs @ 176°F, with Aced Etched 6061-T6 Aluminum
Peel Strength 7.01 kN/m
40.0 pli
Cure cycle: 1 day @ RT, with Acid Etched 6061-T6 Aluminum
7.01 kN/m
40.0 pli
Cure cycle: 12 hrs @ RT + 1 hr @ 176°F, with Acid Etched 6061-T6 Aluminum
7.01 kN/m
40.0 pli
Cure cycle: 3 days @ RT, with Acid Etched 6061-T6 Aluminum