Polymer Property : Linear Mold Shrinkage, Transverse = 0.0073 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Transverse	0.0073 cm/cm @Time 86400 sec	0.0073 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP ZFG26 PPE+PS LNP* LUBRICOMP* ZFG26 is a compound based on PPE+PS resin containing 30% Glass Fiber, 10% Graphite. Added features of this material include: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.0073 cm/cm @Time 86400 sec	0.0073 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP ZFG26 PPE+PS (Asia Pacific) LNP* Lubricomp* ZFG26 is a compound based on PPE+PS Blend resin containing Glass Fiber, Graphite Powder. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0073 cm/cm @Time 86400 sec	0.0073 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP LC008E PEEK LNP* THERMOCOMP* LC008E is a compound based on Polyetheretherketone resin containing 40% Carbon Fiber. Added features of this material include: Easy Molding, Electrically Conductive.
Linear Mold Shrinkage, Transverse	0.0073 cm/cm @Time 86400 sec	0.0073 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP LC008E PEEK (Asia Pacific) LNP* Thermocomp* LC008E is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added features of this material include: Easy Molding, Electrically Conductive.
Linear Mold Shrinkage, Transverse	0.0073 cm/cm @Time 86400 sec	0.0073 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP QFL17RS PA 6/10 LNP LUBRICOMP* QFL17RS is a compound based on Nylon 6/10 resin containing 35% Glass Fiber, 5% PTFE. Added features of this material include: Easy Release, Heat Stabilized, Wear Resistant.
Linear Mold Shrinkage, Transverse	0.0073 cm/cm @Time 86400 sec	0.0073 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP DB008ERP PC LNP* THERMOCOMP* DB008ERP is a compound based on Polycarbonate resin containing 40% Glass Bead. Added features of this material include: Easy Molding, Mold Release.
Linear Mold Shrinkage, Transverse	0.0073 cm/cm @Time 86400 sec	0.0073 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP DB008ERP PC (Asia Pacific) LNP* Thermocomp* DB008ERP is a compound based on Polycarbonate resin containing Glass Bead. Added features of this material include: Easy Molding, Mold Release.
Linear Mold Shrinkage, Transverse	0.0073 cm/cm @Time 86400 sec	0.0073 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP SF008 PA 12 LNP* THERMOCOMP* SF008 is a compound based on Nylon 12 resin containing 40% Glass Fiber.
Linear Mold Shrinkage, Transverse	0.0073 cm/cm @Time 86400 sec	0.0073 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP SF008 PA 12 (Asia Pacific) LNP* Thermocomp* SF008 is a compound based on Nylon 12 resin containing Glass Fiber.