Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 2.9 - 3.2 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.9 - 3.2 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238/L |
NIZHNEKAMSKNEFTEKHIM PP 1525J (T28F) Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
Melt Flow | 2.6 - 3.2 g/10 min | 2.6 - 3.2 g/10 min | ±10% |
Kazanorgsintez 276-288 High Density Polyethylene Composite Production Method: Compositions are achieved by gaseous-phase method. Application: Composition is intended for production of polymer film fibers contacting bulk food.Information Provided by Kaza.. |
|||
Melt Flow | 2.6 - 3.2 g/10 min | 2.6 - 3.2 g/10 min | ±18% |
Kazanorgsintez 295-73 High Density Polyethylene Composite Production Method: Compositions are achieved by ethylene copolymerization by gaseous-phase method at low pressure using complex catalysts on carrier material. Application: Composition of HD grad.. |
|||
Melt Flow | 2.4 - 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.4 - 3.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
Ipiranga Petrochem LB 0316 LLDP IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba.. |