Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 8.4 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.4 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 7 cm<sup>3</sup>/10min.; ISO 1133 |
Mitsubishi Xantar® 24 R Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Melt Flow | 8.4 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.4 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 7 cm<sup>3</sup>/10min.; ISO 1133 |
Mitsubishi Xantar® 24 SR FD Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Melt Flow | 8.4 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.4 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 7 cm<sup>3</sup>/10min.; ISO 1133 |
Mitsubishi Xantar® 24 UR Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Melt Flow | 8.4 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.4 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 7 cm<sup>3</sup>/10min.; ISO 1133 |
Mitsubishi Xantar® F 23 UR Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Melt Flow | 8.4 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.4 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 7 cm<sup>3</sup>/10min.; ISO 1133 |
Mitsubishi Xantar® FC 23 UR Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Melt Flow | 8.4 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.4 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 7 cm<sup>3</sup>/10min.; ISO 1133 |
Mitsubishi Xantar® F 23 R Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Melt Flow | 8.4 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.4 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 7 cm<sup>3</sup>/10min.; ISO 1133 |
Mitsubishi Xantar® FC 23 R Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Melt Flow | 8.4 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.4 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 7 cm<sup>3</sup>/10min.; ISO 1133 |
Mitsubishi Xantar® MX 2015 Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Melt Flow | 8.4 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.4 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 7 cm<sup>3</sup>/10min.; ISO 1133 |
Mitsubishi Xantar® MX 2042 FD Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Melt Flow | 8.4 g/10 min @Load 6.60 kg, Temperature 337 °C |
8.4 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
SABIC Innovative Plastics ULTEM 2210 PEI 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. |
|||
Melt Flow | 8.4 g/10 min @Load 6.60 kg, Temperature 337 °C |
8.4 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
SABIC Innovative Plastics ULTEM 2210 PEI (Asia Pacific) 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. |
|||
Melt Flow | 8.4 g/10 min @Load 6.60 kg, Temperature 337 °C |
8.4 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
SABIC Innovative Plastics ULTEM HU2210 PEI 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP .. |
|||
Melt Flow | 8.4 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.4 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
Teijin Panlite® L-1250ZW Extrusion Grade Polycarbonate Resin Information provided by Teijin Chemicals Ltd. |
|||
Melt Flow | 8.4 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.4 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil Escor™ 5050 ExCo Ethylene Acrylic Acid Copolymer Resin Product Description: Escor 5050 is primarily intended for extrusion coating, coextrusion coating and extrusion lamination. Outstanding adhesion to polar substrates, aluminum foil, metalized films, p.. |
|||
Melt Flow | 8.4 g/10 min @Load 5.00 kg, Temperature 280 °C |
8.4 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
SABIC Innovative Plastics NORYL ENG265 PPE+PS PPE+PS blend. Unfilled. Suitable for profile extrusion. NSF listed for potable water use in several colors (Standard 61). Low water absorption. Hydrolytic stability. Dimensional stability. Typical a.. |