Physical Properties | Metric | English | Comments |
---|---|---|---|
Oxygen Transmission | 197 cc-mm/m²-24hr-atm @Thickness 0.0254 mm |
500 cc-mil/100 in²-24hr-atm @Thickness 0.00100 in |
Based on 1 mil (0.0254 mm) thick film; ASTM D3985 |
DuPont Elvax® 3150 Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Blown Film 15 wt% Vinyl Acetate.General Elvax® information: Elvax® packaging grade resins include low seal temperatures for use in coextrusions or for packaging temperature sensitive materials, excellent dra.. |
|||
Oxygen Transmission | 197 - 200 cc-mm/m²-24hr-atm | 500 - 508 cc-mil/100 in²-24hr-atm | Average value: 199 cc-mm/m²-24hr-atm Grade Count:5 |
Overview of materials for Low Density Polyethylene (LDPE), Molded This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Molded". Each property range of values reported is minimum and maximum .. |
|||
Oxygen Transmission | 197 cc-mm/m²-24hr-atm @Thickness 0.0254 mm |
500 cc-mil/100 in²-24hr-atm @Thickness 0.00100 in |
Based on 1 mil (0.0254 mm) thick film; ASTM D3985 |
DuPont Elvax® 3128 Ethylene-Vinyl Acetate Copolymer Resin for Blown Film
(discontinued **) 8.9 wt% Vinyl Acetate.Elvax® 3128 is an extrudable ethylene-vinyl acetate copolymer resin available in pellet form for use in conventional extrusion equipment designed to process polyethylene resin.. |
|||
Oxygen Transmission | 197 cc-mm/m²-24hr-atm | 500 cc-mil/100 in²-24hr-atm | Based on 1 mil (0.0254 mm) thick film; ASTM D3985 |
DuPont Elvax® 3169 Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Blown Film
(discontinued **) 18 wt% Vinyl Acetate.General Elvax® information: Elvax® packaging grade resins include low seal temperatures for use in coextrusions or for packaging temperature sensitive materials, excellent dra.. |