Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Flow	0.0083 cm/cm @Time 86400 sec	0.0083 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP DL003 PC LNP LUBRICOMP* DL003 is a compound based on Polycarbonate resin containing 15% PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.0083 cm/cm @Time 86400 sec	0.0083 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP DL003 PC (Asia Pacific) LNP LUBRICOMP* DL003 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.0083 cm/cm @Time 86400 sec	0.0083 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP ZL003 PPE+PS LNP* LUBRICOMP* ZL003 is a compound based on PPE+PS resin containing 15% PTFE. Added features of this material include: Wear Resistant.
Linear Mold Shrinkage, Flow	0.0083 cm/cm @Time 86400 sec	0.0083 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP ZL003 PPE+PS (Asia Pacific) LNP LUBRICOMP ZL003 is a compound based on PPE+PS Blend resin containing PTFE. Added features of this material include:internally Lubricated. Also known as LUBRICOMP ZL-4030
Linear Mold Shrinkage, Flow	0.0083 cm/cm @Time 86400 sec	0.0083 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP WFB54 PBT LNP* THERMOCOMP* WFB54 is a compound based on PBT resin containing 20% Glass Fiber, 25% Glass Bead.
Linear Mold Shrinkage, Flow	0.0083 cm/cm @Time 86400 sec	0.0083 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP WFB54 PBT (Asia Pacific) LNP* Thermocomp* WFB54 is a compound based on Polybutylene Terephalate resin containing Glass Bead.