Polymer Property : Linear Mold Shrinkage, Flow = 0.019 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Flow	0.019 cm/cm @Thickness 4.00 mm	0.019 in/in @Thickness 0.157 in
DuPont Performance Polymers Delrin® 100TL NC010 Acetal Homopolymer (Unverified Data**) Delrin® 100TL NC010 is a high viscosity acetal homopolymer with 1.5% Teflon® PTFE Micropowder.Information provided by DuPont Performance Polymers
Linear Mold Shrinkage, Flow	0.019 cm/cm @Thickness 4.00 mm	0.019 in/in @Thickness 0.157 in	ISO 294-4
DuPont Performance Polymers Delrin® 500AL NC010 Acetal Homopolymer (Unverified Data**) Delrin® 500AL is a medium viscosity acetal homopolymer, with an advanced system of lubrication for applications requiring low wear and/or coefficient of friction against steel, itself or other plas..
Linear Mold Shrinkage, Flow	0.019 - 0.021 cm/cm @Time 86400 sec	0.019 - 0.021 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Lubricomp QP003 PA 6/10 LNP* Lubricomp* QP003 is a compound based on Nylon 6/10 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Am..
Linear Mold Shrinkage, Flow	0.019 - 0.021 cm/cm @Time 86400 sec	0.019 - 0.021 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Lubricomp QP003 PA 6/10 (Asia Pacific) LNP* Lubricomp* QP003 is a compound based on Nylon 6/10 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the As..
Linear Mold Shrinkage, Flow	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RAL22 PA 66 LNP LUBRICOMP* RAL22 is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant.
Linear Mold Shrinkage, Flow	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RAL22 PA 66 (Asia Pacific) LNP LUBRICOMP* RAL22 is a compound based on Nylon 66 resin containing Aramid, PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RAL22S PA 66 LNP* LUBRICOMP* RAL22S is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant.
Linear Mold Shrinkage, Flow	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RAL22S PA 66 (Asia Pacific) LNP* Lubricomp* RAL22S is a compound based on Nylon 66 resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RL0019 PA 66 LNP LUBRICOMP* RL0019 is a compound based on Nylon 66 resin containing 5% PTFE. Added features of this material include: Flame Retardant, Wear Resistant.
Linear Mold Shrinkage, Flow	0.019 - 0.033 cm/cm @Time 86400 sec	0.019 - 0.033 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RL004S PA 66 LNP LUBRICOMP* RL004S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant.
Linear Mold Shrinkage, Flow	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RP004 PA 66 (Asia Pacific) LNP* Lubricomp* RP004 is a compound based on Nylon 66 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP RP004 PA 66 (Asia Pacific) LNP* Lubricomp* RP004 is a compound based on Nylon 66 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP KFB11 Acetal Copoly LNP* THERMOCOMP* KFB11 is a compound based on Acetal Copolymer resin containing 5% Glass Fiber, 5% Glass Bead. Added features of this material include: Low Warpage, Chemically Coupled.
Linear Mold Shrinkage, Flow	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-LOY KX96821 Acetal LNP STAT-LOY* KX96821 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Antistat.
Linear Mold Shrinkage, Flow	0.019 cm/cm @Thickness 4.00 mm	0.019 in/in @Thickness 0.157 in
DuPont Performance Polymers Delrin® FG100TL NC010 Acetal Homopolymer (Unverified Data**) Delrin® 100TL is a high viscosity acetal homopolymer, containing 1.5% Teflon® PTFE Micropowder. It has been developed for consideration into applications such as parts for the food industry.Inform..
Linear Mold Shrinkage, Flow	0.019 cm/cm @Time 86400 sec	0.019 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP KFB11 Acetal Copoly (Asia Pacific) LNP* Thermocomp* KFB11 is a compound based on Acetal Copolymer resin containing Glass Fiber, Milled Glass. Added features of this material include: Low Warpage, Chemically Coupled.