Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 115 MPa | 16700 psi | at Yield; ISO 527-1/-2 |
Quadrant EPP Ketron® 1000 PEEK unfilled, extruded (ISO Data) Ketron PEEK-1000 stock shapes are produced from virgin polyetheretherketone resin and offer the highest toughness and impact strength of all Ketron PEEK grades. Both Ketron PEEK-1000 natural & black.. |
|||
Tensile Strength | 115 MPa @Thickness 4.00 mm, Temperature 23.0 °C |
16700 psi @Thickness 0.157 in, Temperature 73.4 °F |
5.0 mm/min; ISO 527 |
PolyOne Bergamid™ B70 G30 BK Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
Tensile Strength | 115 MPa | 16700 psi | at Break (NYP); ISO 527-1/-2 |
Quadrant EPP Duratron® PI D7000 PI, unfilled (ISO Data) Duratron D7000 PI – the basic grade within the Duratron PI family – is made from unfilled polyimide resin and provides maximum physical properties and best electrical and thermal insulation. Good .. |
|||
Tensile Strength | 115 MPa | 16700 psi | 5 mm/min; ISO 527-1 |
Sax Polymers SAXAMID 236F4Q32 Nylon 6.6, 20% Glass Fiber SAXAMID 236 F4Q32 is a impact-modified polyamide 6.6 injection-molding-grade reinforced with 20% glass fibers and very good flow properties. It is suitable for applications requiring toughness in co.. |
|||
Tensile Strength | 115 MPa | 16700 psi | ISO 527-1/-2 |
Murtfeldt Murpec® Polyetheretherketone In comparison with other thermoplastics, Murpec® has an exceptionally low thermal expansion coefficient. This property provides optimum dimensional stability and means that dimensions do not change.. |