Mechanical Properties | Metric | English | Comments |
---|---|---|---|
100% Modulus | 0.00570 GPa | 0.827 ksi | TPE-0153 (ASTM D 412) |
Advanced Elastomer Systems Santoprene® 253-36 Thermoplastic Rubber
(discontinued **) A colorable thermoplastic flame retardant elastomer with good fluid resistance, formulated to replace thermoset elastomers such as EPDM, polychloroprene, and chlorosulfonated polyethylene. It can b.. |
|||
100% Modulus | 0.00570 GPa | 0.827 ksi | ASTM D412 |
DuPont Vamac® G/HVG Sample Compound
(discontinued **) Test compound is press cured for 5 minutes at 175°C and post cured for 4 hours at 175°C.Information provided by DuPont. |
|||
100% Modulus | 0.00570 GPa | 0.827 ksi | DIN 53504 |
Huntsman IROGRAN® A 80 P 4699L Ether-Based TPU-For Cable Industry Introduction: IROGRAN A 80 P 4699 L is a high performance polyether based thermoplastic polyurethane intended for extrusion and injection mold applications. IROGRAN A 80 P 4699 L is part of the HUNT.. |
|||
100% Modulus | 0.00570 GPa | 0.827 ksi | DIN 53504 |
Lubrizol ESTANE® 5713 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
100% Modulus | 0.00570 GPa @Temperature 23.0 °C |
0.827 ksi @Temperature 73.4 °F |
12 months, Weathering @ 45° South, 12 mil - Black, Florida |
Lubrizol Estane® 58610 Thermoplastic Polyurethane Features: Combines flexibility, toughness and excellent roll release for calendering and melt coating applications.Uses: Injection molding and general extrusion techniques. It is used in film, shee.. |
|||
100% Modulus | 0.00570 GPa | 0.827 ksi | DIN 53504 |
Lubrizol ESTANE® 58562 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |