Mechanical Properties	Metric	English	Comments
Tensile Creep Modulus, 1 hour	2400 MPa @Temperature 23.0 °C	348000 psi @Temperature 73.4 °F	ISO 899
DuPont Performance Polymers Delrin® FG500AL NC010 Acetal Homopolymer (Unverified Data**) Delrin® FG500AL is a medium viscosity acetal homopolymer, lubricated for low wear and /or coefficient of friction. It has been developed for consideration into applications such as parts for the fo..
Tensile Creep Modulus, 1 hour	2400 MPa	348000 psi	ISO 899-1
Lanxess DurethanÂ® BG 30 X 000000 Nylon 6, 30% Glass Fiber PA 6, injection molding grade, 30% glass fibers/glass spheres, good surface, low warpage
Tensile Creep Modulus, 1 hour	2400 MPa	348000 psi	Conditioned; ISO 889-1
Lanxess DurethanÂ® BG 30 X H3.0 000000 Nylon 6, 30% Glass Fibers/Glass Spheres PA 6, 30% glass fibers/glass spheres, injection molding, heat-ageing stabilized, low tendency to warp
Tensile Creep Modulus, 1 hour	2400 MPa	348000 psi	ISO 899-1
Lanxess PocanÂ® B 1300 000000 PBT PBT, non-reinforced, injection molding, extrusion
Tensile Creep Modulus, 1 hour	2400 MPa	348000 psi	ISO 899-1
Lanxess PocanÂ® B 1305 000000 PBT PBT, non-reinforced, injection molding
Tensile Creep Modulus, 1 hour	2400 MPa	348000 psi	ISO 899-1
Lanxess PocanÂ® KU 2-7003 000000 PBT PBT, non-reinforced, injection molding
Tensile Creep Modulus, 1 hour	2400 MPa	348000 psi	ISO 899-1
Lanxess PocanÂ® KU 2-7503/1 000000 PBT PBT, non-reinforced, injection molding, extrusion, flame retardant
Tensile Creep Modulus, 1 hour	2400 MPa @Time 3600 sec	348000 psi @Time 1.00 hour	ISO 899-1
DuPont Performance Polymers Delrin® 500AL NC010 Acetal (POM) (Unverified Data**) Lubricated Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction Delrin 500AL is a medium viscosity acetal homopolymer with an advanced system of lubrication for applications requiring ..
Tensile Creep Modulus, 1 hour	2400 MPa @Time 3600 sec	348000 psi @Time 1.00 hour	ISO 899-1
DuPont Performance Polymers Delrin® FG500AL NC010 Acetal (POM) (Unverified Data**) Lubricated Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction Developed for Food Contact Applications Delrin FG500AL is a medium viscosity acetal homopolymer lubricated for low wear ..
Tensile Creep Modulus, 1 hour	2400 MPa	348000 psi
Ineos ABS NOVODUR® P2T ABS, Injection Grade (discontinued **) Injection molding grade, very high heat resistance.Applications: Automotive industry, household appliances.Information provided by the manufacturer.Novodur is produced by Styrolution (2014). This g..
Tensile Creep Modulus, 1 hour	2400 MPa	348000 psi
Arkema Group Oroglas® VS-UVT Acrylic, Injection Molding Grade (discontinued **) The outstanding flow of OROGLAS VS-UVT makes it as the material of choice for injection molding of part with thin wall thickness.The ultraviolet transmitting ( uvt) formulation is developed to meet ..