Polymer Property : Modulus of Elasticity = 20500 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Modulus of Elasticity	141 GPa @Temperature 982 Â°C	20500 ksi @Temperature 1800 Â°F
Haynes HastelloyÂ® C-4 alloy, all-weld metal, as welded, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Modulus of Elasticity	141 GPa @Temperature 982 Â°C	20500 ksi @Temperature 1800 Â°F
Haynes HastelloyÂ® C-4 alloy, plate, heat treated at 1066Â°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Modulus of Elasticity	141 GPa @Temperature 982 Â°C	20500 ksi @Temperature 1800 Â°F
Haynes HastelloyÂ® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours at 649Â°C (1200Â°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Modulus of Elasticity	141 GPa @Temperature 593 °C	20500 ksi @Temperature 1100 °F
Crucible Steel 422 Stainless Steel Crucible 422 is a hardenable martensitic stainless steel which is being widely used for high temperatures up to 1200°F. It has excellent creep-rupture properties in the range of 600/1200°F and is..
Modulus of Elasticity	141 GPa	20500 ksi
Carpenter Invar 36® Alloy, Annealed Bars and Strip Data provided by Carpenter Technology Corporation.Carpenter Invar "36" alloy is a 36% nickel-iron alloy possessing a rate of thermal expansion approx. one-tenth that of carbon steel up to 200°C. T..
Modulus of Elasticity	141 GPa @Temperature 982 °C	20500 ksi @Temperature 1800 °F
Haynes Hastelloy® C-4 alloy, sheet, aged 100 hours at 899°C Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..
Modulus of Elasticity	141 GPa @Temperature 982 °C	20500 ksi @Temperature 1800 °F
Haynes Hastelloy® C-4 alloy, sheet, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..
Modulus of Elasticity	141 GPa @Temperature 982 °C	20500 ksi @Temperature 1800 °F
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 10 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..
Modulus of Elasticity	141 GPa @Temperature 982 °C	20500 ksi @Temperature 1800 °F
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..