Polymer Property : Modulus of Elasticity = 210 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	210 GPa @Diameter 15.9 mm, Temperature 23.0 Â°C	30500 ksi @Diameter 0.626 in, Temperature 73.4 Â°F	bar
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, 12.7 mm (1/2 in.) thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Modulus of Elasticity	210 GPa @Diameter 15.9 mm, Temperature 23.0 Â°C	30500 ksi @Diameter 0.626 in, Temperature 73.4 Â°F	bar
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816Â°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Modulus of Elasticity	210 GPa	30500 ksi
H.C. Starck MoCu 70/30 Molybdenum-Copper Composite Material Description of Product: Molybdenum-copper composite materials are produced by copper infiltration of porous sintered molybdenum. They are available with different copper contents (15 - 35 %). A t..
Modulus of Elasticity	210 GPa @Temperature 100 Â°C	30500 ksi @Temperature 212 Â°F
Haynes 214Â® alloy, 0% cold reduction Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	210 GPa @Temperature 100 Â°C	30500 ksi @Temperature 212 Â°F
Haynes 214Â® alloy, 20% cold reduction Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	210 GPa @Temperature 100 Â°C	30500 ksi @Temperature 212 Â°F
Haynes 214Â® alloy, 30% cold reduction, 925Â°C for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	210 GPa @Temperature 100 Â°C	30500 ksi @Temperature 212 Â°F
Haynes 214Â® alloy, sheet, 100 hours exposure at 760Â°C (1400Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	210 GPa @Temperature 100 Â°C	30500 ksi @Temperature 212 Â°F
Haynes 214Â® alloy, sheet, 100 hours exposure at 870Â°C (1600Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	210 GPa @Temperature 100 Â°C	30500 ksi @Temperature 212 Â°F
Haynes 214Â® alloy, sheet, 32 hours exposure at 980Â°C (1800Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	210 GPa @Temperature 40.0 Â°C	30500 ksi @Temperature 104 Â°F
Haynes HR-160Â® alloy plate, aged 1000 hours at 649Â°C (1200Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Modulus of Elasticity	210 GPa	30500 ksi
Latrobe LescalloyÂ® D6AC VAC-ARC High Strength Alloy Steel LESCALLOY D6AC VAC-ARC steel is a medium carbon, low alloy, ultra high strength steel primarily designed for high strength structural applications requiring strength leaves up to 280,000 psi. This ..
Modulus of Elasticity	210 GPa @Temperature 40.0 Â°C	30500 ksi @Temperature 104 Â°F
Haynes HR-160Â® alloy, annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Modulus of Elasticity	210 GPa @Temperature 40.0 Â°C	30500 ksi @Temperature 104 Â°F
Haynes HR-160Â® alloy, hot rolled and solution annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Modulus of Elasticity	210 GPa @Temperature 100 Â°C	30500 ksi @Temperature 212 Â°F
Haynes 214Â® alloy, 10% cold reduction, 1095Â°C (2000Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	210 GPa @Temperature 40.0 Â°C	30500 ksi @Temperature 104 Â°F
Haynes HR-160Â® alloy plate, aged 8000 hours at 649Â°C (1200Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Modulus of Elasticity	210 GPa	30500 ksi	Dynamic Method
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 2 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness Tensile strength (ultimate and yield), shear strength, and elongation values reported here are typical for Cold Rolled Sheet, 2 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness samples. Density a..
Modulus of Elasticity	210 GPa	30500 ksi	Dynamic Method
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 3 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness Tensile strength (ultimate and yield), shear strength, and elongation values reported here are typical for Cold Rolled Sheet, 3 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness samples. Density a..
Modulus of Elasticity	210 GPa	30500 ksi	Dynamic Method
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 3 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness Tensile and bearing strengths (ultimate and yield) and elongation values reported here are typical for Cold Rolled Sheet, 3 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness samples. Density and m..
Modulus of Elasticity	210 GPa	30500 ksi	Precipitation Hardened, Dynamic Method
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, Solution Treated Tensile strength (ultimate and yield), and elongation values reported here are typical for Cold Rolled Sheet, Solution Treated samples. Density and magnetic permeability are typical of annealed INCO..
Modulus of Elasticity	210 GPa	30500 ksi	Dynamic Method
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Hot Finished Flat, 2 Part Heat Treatment, 1.250 inch (31.8 mm) Thickness Tensile strength (ultimate and yield), shear strength, compressive strength, reduction of area, and elongation values reported here are typical for Hot Finished Flat, 2 Part Heat Treatment, 1.250 in..
Modulus of Elasticity	210 GPa	30500 ksi
Special Metals NIMONICÂ® Alloy 86 A nickel-chromium-molybdenum alloy with a rare-earth (cerium) addition. It combines good formability and weldability with exceptional resistance to oxidation and scaling at temperatures to 1920Â°..
Modulus of Elasticity	210 GPa	30500 ksi	ASTM C848
CoorsTek Yttria Partially Stabilized Zirconia, YZTP, Sintered Thermal Shock Delta Tc = 350°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar..
Modulus of Elasticity	210 GPa	30500 ksi	ASTM C848
CoorsTek YZTP Yttria Partially Stabilized Zirconia, Hipped Thermal Shock Delta Tc = 350°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar..
Modulus of Elasticity	210 GPa	30500 ksi	(hardness of 45 HRC)
Bohler-Uddeholm UDDEHOLM ORVAR® SUPERIOR (Premium AISI H13) Hot Work Tool Steel Chromium-molybdenum-vanadium alloyed steelA premium Cr-Mo-V-alloyed hot work die steel with good resistance to thermal fatigue. The steel is produced by a special melting and refining technique in o..
Modulus of Elasticity	210 GPa @Diameter 15.9 mm, Temperature 23.0 °C	30500 ksi @Diameter 0.626 in, Temperature 73.4 °F	bar
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..