- Polymer Property : Modulus of Elasticity = 28900 ksi
Polymer Property : Modulus of Elasticity = 28900 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 199 GPa @Temperature 300 °C |
28900 ksi @Temperature 572 °F |
|
| Haynes 214® alloy, 0% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 300 °C |
28900 ksi @Temperature 572 °F |
|
| Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 300 °C |
28900 ksi @Temperature 572 °F |
|
| Haynes 214® alloy, sheet, 100 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 300 °C |
28900 ksi @Temperature 572 °F |
|
| Haynes 214® alloy, sheet, 100 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 300 °C |
28900 ksi @Temperature 572 °F |
|
| Haynes 214® alloy, sheet, 1000 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 300 °C |
28900 ksi @Temperature 572 °F |
|
| Haynes 214® alloy, sheet, 32 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 300 °C |
28900 ksi @Temperature 572 °F |
|
| Haynes 214® alloy, 10% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 300 °C |
28900 ksi @Temperature 572 °F |
|
| Haynes 214® alloy, 30% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 500 °C |
28900 ksi @Temperature 932 °F |
|
| Haynes 242® alloy, after 1000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 500 °C |
28900 ksi @Temperature 932 °F |
|
| Haynes 242® alloy, after 8000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 500 °C |
28900 ksi @Temperature 932 °F |
|
| Haynes 242® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 500 °C |
28900 ksi @Temperature 932 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 500 °C |
28900 ksi @Temperature 932 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 500 °C |
28900 ksi @Temperature 932 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and 40% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 500 °C |
28900 ksi @Temperature 932 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 500 °C |
28900 ksi @Temperature 932 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed, 40% cold work, aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 500 °C |
28900 ksi @Temperature 932 °F |
|
| Haynes 242® alloy, cold rolled sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 200 °C |
28900 ksi @Temperature 392 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 200 °C |
28900 ksi @Temperature 392 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 200 °C |
28900 ksi @Temperature 392 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 200 °C |
28900 ksi @Temperature 392 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 200 °C |
28900 ksi @Temperature 392 °F |
|
| Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 200 °C |
28900 ksi @Temperature 392 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 200 °C |
28900 ksi @Temperature 392 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 200 °C |
28900 ksi @Temperature 392 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 200 °C |
28900 ksi @Temperature 392 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 100 °C |
28900 ksi @Temperature 212 °F |
|
| Haynes 718 alloy, cold rolled, solution-treated and aged sheet Cb and Ta content combined weight percentage of 5. Excellent high-temperature strength up to 650°C, good ductility, formability, and weldability. Very good welding characteristics. Applications i.. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 200 °C |
28900 ksi @Temperature 392 °F |
|
| Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 200 °C |
28900 ksi @Temperature 392 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Modulus of Elasticity | 199 GPa @Temperature 200 °C |
28900 ksi @Temperature 392 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||