- Polymer Property : Modulus of Elasticity = 151 GPa
Polymer Property : Modulus of Elasticity = 151 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 151 GPa @Temperature 904 °C |
21900 ksi @Temperature 1660 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 904 °C |
21900 ksi @Temperature 1660 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 904 °C |
21900 ksi @Temperature 1660 °F |
|
| Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, gas tungsten arc welded Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged at 538°C (1000°F) for 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, weld metal, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, weld metal, aged at 649°C (1200°F) for 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 904 °C |
21900 ksi @Temperature 1660 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 904 °C |
21900 ksi @Temperature 1660 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 904 °C |
21900 ksi @Temperature 1660 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 904 °C |
21900 ksi @Temperature 1660 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 904 °C |
21900 ksi @Temperature 1660 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Modulus of Elasticity | 151 GPa @Temperature 927 °C |
21900 ksi @Temperature 1700 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||