Polymer Property : Modulus of Elasticity = 166 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, flat products Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 538Â°C (1000Â°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 538Â°C (1000Â°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 538Â°C (1000Â°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 538Â°C (1000Â°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 649Â°C (1200Â°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 649Â°C (1200Â°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 649Â°C (1200Â°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 760Â°C (1400Â°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, gas tungsten arc welded Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649Â°C (1200Â°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, gas tungsten arc welded, aged 1300 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427Â°C (800Â°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427Â°C (800Â°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, weld metal, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 760 Â°C	24100 ksi @Temperature 1400 Â°F	Heat treated at 1066Â°C, air cooled
Haynes HastelloyÂ® S alloy, weld metal, aged at 649Â°C (1200Â°F) for 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity	166 GPa @Temperature 816 Â°C	24100 ksi @Temperature 1500 Â°F
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Modulus of Elasticity	166 GPa @Temperature 816 Â°C	24100 ksi @Temperature 1500 Â°F
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1121Â°C, air cooled, aged 16 hours at 899Â°C Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Modulus of Elasticity	166 GPa @Temperature 800 Â°C	24100 ksi @Temperature 1470 Â°F	Dynamic
Haynes 282Â® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Modulus of Elasticity	166 GPa @Temperature 800 Â°C	24100 ksi @Temperature 1470 Â°F	Dynamic
Haynes 282Â® Nickel Alloy Sheet, Solution Annealed and Cold Worked Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Modulus of Elasticity	166 GPa @Temperature 800 Â°C	24100 ksi @Temperature 1470 Â°F	Dynamic
Haynes 282Â® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Modulus of Elasticity	166 GPa @Temperature 760 °C	24100 ksi @Temperature 1400 °F	Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Modulus of Elasticity	166 GPa @Temperature 760 °C	24100 ksi @Temperature 1400 °F	Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Modulus of Elasticity	166 GPa @Temperature 760 °C	24100 ksi @Temperature 1400 °F	Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Modulus of Elasticity	166 GPa @Temperature 800 °C	24100 ksi @Temperature 1470 °F	Dynamic
Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b..
Modulus of Elasticity	166 GPa @Temperature 700 °C	24100 ksi @Temperature 1290 °F	Dynamic
Haynes 617 Nickel Alloy Plate Haynes 617 alloy is a nickel-chromium-cobalt-molybdenum alloy with a good combination of metallurgical stability, strength, and oxidation resistance at high temperatures. The alloy is readily formed..
Modulus of Elasticity	166 GPa @Temperature 760 °C	24100 ksi @Temperature 1400 °F	Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..