Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 214 MPa | 31000 psi | 1.3 mm/min; ASTM D790 |
PolyOne LubriOne™ CTX-502 Natural Polyether Imide (PEI) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
Polymer Resources NY66-IMG33-[color]H Nylon, 33% Glass Reinforced, Impact Modified, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
Techmer ES HiFill® PA6/6 G/CF30 L BK 30% GlassCarbon Filler Availability: North AmericaForms: PelletsFiller/Reinforcement: GlassCarbon Fiber Reinforcement, 30% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedApp.. |
|||
Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
Techmer ES HiFill® PA6/6 GF25 HS L 25% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 25% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Lubricated and Heat StabilizedProcessin.. |
|||
Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
Techmer ES HiFill® PA6/6 GF25 HS L BK 25% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 25% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Lubricated and Heat StabilizedAppearanc.. |
|||
Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
Techmer ES HiFill® PA6/6 GF30 L 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
Techmer ES HiFill® PA6/6 GF30 LE 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightFeatures: Low ExtractablesInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
Techmer ES HiFill® PA6/6 GF33 HS L BK 33% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedAppearanc.. |
|||
Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
Techmer ES Plaslube® J-4/35/TF/15 NAT PA6/12 |
|||
Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
Techmer ES HiFill® PBT G/CF30 15% Glass/Carbon Filler Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Carbon Fiber Reinforcement, 15% Filler by WeightAppearance: Natural ColorInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 214 MPa | 31000 psi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp XF006S LNP* Thermocomp* XF006S is a compound based on Amorphous Nylon containing Glass Fiber. Characteristics of this grade are: Heat Stabilized.This data was supplied by SABIC-IP for the Americas region.. |
|||
Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
Adell AR-34 Nylon 66, 20% Glass Reinforced Data provided by Adell Plastics, Inc. |
|||
Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
A. Schulman ComAlloy Lubrilon® 629 Nylon 6/6, Glass Fiber/PTFE Filled, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma.. |
|||
Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
Chase Plastics CP Pryme® NN133GTL (DAM) Nylon 66, 33% Glass Fiber Reinforced, Toughened, Internally Lubricated Information provided by Chase Plastics. |
|||
Flexural Strength | 214 MPa | 31000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON QEP35M PA6.10 LNP STAT-KON QEP35M is a compound based on Nylon 6/10 resin containing 25% Milled Carbon Fiber, 15% PTFE/Silicone. Added features of this grade include: Electrically Conductive, Wear Resistant. |
|||
Flexural Strength | 214 MPa | 31000 psi | ISO 178 |
SABIC Innovative Plastics LNP VERTON MV00ASU PP (Asia Pacific) LNP VERTON* MV00ASU is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. |