Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 165 MPa | 24000 psi | ASTM D790 |
Niche Polymer PA66GI14BK Nylon 66, 14% Glass Fiber Filled, Impact Modified Information provided by Niche Polymer |
|||
Flexural Strength | 165 MPa | 24000 psi | ASTM D790 |
Quadrant EPP Duratron® PAI T4203 Extruded Polyamide-imide (ASTM Product Data Sheet) |
|||
Flexural Strength | 165 MPa | 24000 psi | ASTM D790 |
Polymer Resources NY6-G13 Nylon 6, 13% Glass Reinforced Nylon 6, 13% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are teste.. |
|||
Flexural Strength | 165 MPa | 24000 psi | ASTM D790 |
Polymer Resources TP-HG40 Polybutylene Terephthalate, 40% Glass Reinforced Alloy Polybutylene Terephthalate, 40% Glass Reinforced AlloyProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informatio.. |
|||
Flexural Strength | 165 MPa | 24000 psi | ASTM D790 |
Ravago Manufacturing Americas Hylon® N1213HL BK Nylon 6/6 Available in North America Filler: Glass Fiber Reinforcement, 13% Filler by WeightAdditive: Heat Stabilizer and Lubricant Features: Lubricated and Heat StabilizedRoHS CompliantForm: Pellets Proces.. |
|||
Flexural Strength | 165 MPa @Thickness 3.17 mm |
24000 psi @Thickness 0.125 in |
LW |
Industrial Laminates/Norplex MC320LE Cotton Fabric Description: Grade MC320LE is a fine weave bleached cotton phenolic composite that has excellent machining characteristics and low moisture absorption. Applications include marine applications, term.. |
|||
Flexural Strength | 165 MPa | 24000 psi | ASTM D790 |
Techmer ES HiFill FR® PBT GF30 FR-S AS 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: AntistaticFeatures: Flame Retardant, Antistatic and Non-BloomingProcessing Method: Injection.. |
|||
Flexural Strength | 165 MPa | 24000 psi | ASTM D790 |
Techmer ES Electrablend® PA6/6 03001 Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber ReinforcementAdditive: Impact Modifier and Heat StabilizerFeatures: Electrically Conductive, Impact Modified and Heat Stab.. |
|||
Flexural Strength | 165 MPa | 24000 psi | ASTM D790 |
Techmer ES HiFill® PC GF20 X 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightAdditive: Mold ReleaseFeatures: Good Mold Release and High FlowInformation provided by T.. |
|||
Flexural Strength | 165 MPa | 24000 psi | ASTM D790 |
A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
Flexural Strength | 165 MPa | 24000 psi | ASTM D790 |
A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
Flexural Strength | 165 MPa | 24000 psi | ASTM D790 |
Applied Composites 150 Polyester SMC Industry Application: TransportationProduct Application: Engine CoversDistinct Features: Grey Pigments Only, Low DensityInformation provided by Applied Composites Corporation. |
|||
Flexural Strength | 165 - 186 MPa | 24000 - 27000 psi | |
Bulk Molding Compounds BMC 810 General Purpose Molding Compound BMC 810 is a general purpose, very high strength compound suitable for compression, transfer and stuffer injection molding. It is characterized by excellent flow and controlled reactivity and is wel.. |