Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
Nilit FRIANYL A63 N-S20 Nylon 6.6 for injection molding Nylon 6.6 for injection molding, low viscosity, impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | <= 58.0 MPa | <= 8410 psi | ISO 178 |
Polykemi AB POLYfill PPH T15040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | <= 58.0 MPa | <= 8410 psi | ISO 178 |
Polykemi AB POLYfill PPH T15040CR Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | <= 58.0 MPa | <= 8410 psi | ISO 178 |
Polykemi AB POLYfill PPH T8040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 58.0 MPa | 8410 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Faradex AS0039 ABS (Europe-Africa-Middle East) LNP* Faradex* AS0039 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding.This .. |
|||
Flexural Strength | 58.0 MPa | 8410 psi | 2mm/min; ASTM D790 |
Kingfa FRABS-518 Flame Retardant ABS Features:UL 94 V-0 @ 1.6-3.0mm, 5VB @ 2.0mmLow temperature impact resistanceApplications:Injection moldingPower tools accessoriesInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
SABIC Innovative Plastics LNP Lubriloy Z2000 PPE+PS LNP* Lubriloy* Z2000 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP fo.. |
|||
Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY Z2000 PPO LNP* LUBRILOY* Z2000 is a compound based on PPO resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON AX00756 ABS LNP STAT-KON* AX00756 is a compound based on ABS resin containing Stainless Steel. Added feature of this material is: Electrically Conductive. |
|||
Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP HB006 PA11 LNP* Thermocomp* HB006 is a compound based on Nylon 11 resin containing 30% Glass Bead. |
|||
Flexural Strength | 58.0 MPa | 8410 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP TF006 PU LNP THERMOCOMP TF006 is a compound based on Polyurethane containing 30% Glass Fiber. |
|||
Flexural Strength | 58.0 MPa | 8410 psi | 3 points and 2 mm/min; ISO 178 |
Styron Magnumâ„¢ 3904 Acrylonitrile Butadiene Styrene (ABS) MAGNUMâ„¢ 3904 is a resin with super-high impact. It is used in a wide range of technical applications. The mass (continuous process) ABS technology of Dow ensures an ABS resin that combines ex.. |
|||
Flexural Strength | 58.0 MPa @Thickness 3.20 mm |
8410 psi @Thickness 0.126 in |
3-points, 2 mm/min, Injection Molded; ISO 178 |
Styron MAGNUMâ„¢ 3904 Acrylonitrile Butadiene Styrene (ABS) Resin Overview: MAGNUMâ„¢ 3904 is a resin with super-high impact. It is used in a wide range of technical applications. It can be processed by injection molding, extrusion or thermoforming. The mass (c.. |
|||
Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
SABIC Innovative Plastics LNP Stat-loy W3000 PBT LNP STAT-LOY* W3000 is a compound based on Polybutylene Terephalate resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americ.. |
|||
Flexural Strength | 58.0 MPa | 8410 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER PC+POLYESTER alloy. Unreinforced, transparent, impact modified for low temperature ductility |
|||
Flexural Strength | 58.0 MPa | 8410 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER (Asia Pacific) PC+POLYESTER alloy. Unreinforced, transparent, impact modified for low temperature ductility |
|||
Flexural Strength | 58.0 MPa | 8410 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER (Europe-Africa-Middle East) PC+POLYESTER alloy. Unreinforced, transparent, impact modified for low temperature ductility |
|||
Flexural Strength | 58.0 MPa | 8410 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1607 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1607 is a 30% talc filled homopolymer polypropylene compound. Information provided by A. Schulman. |
|||
Flexural Strength | 58.0 MPa | 8410 psi | ASTM D790 |
Plenco 7203 Phenolic, Granular, Transfer Molded PLENCO 07203 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength and an industrial finish. UL recognized under component file E40654. 07203 is available i.. |
|||
Flexural Strength | 58.0 MPa | 8410 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1607 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1607 is a 30% talc filled homopolymer polypropylene compound. Information provided by A. Schulman. |
|||
Flexural Strength | 58.0 MPa | 8410 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1607 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1607 is a 30% talc filled homopolymer polypropylene compound. Information provided by A. Schulman. |
|||
Flexural Strength | 58.0 MPa | 8410 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1607 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1607 is a 30% talc filled homopolymer polypropylene compound. Information provided by A. Schulman. |
|||
Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
Breplast Bretene PP Polypropylene Composite Recovered polypropylene compositeInformation provided by Breplast S.p.A. |
|||
Flexural Strength | 58.0 MPa | 8410 psi | ISO 178 |
Cathay PA512 Renewable Engineering Polyamide Cathay engineering polyamides contain 26-100% renewably sourced material. Advantages: Operates at similar conditions to PA66; Suitable for injection, compounding and extrusion; Stable mechanical pr.. |
|||
Flexural Strength | 58.0 - 76.0 MPa @Strain 5.00 % |
8410 - 11000 psi @Strain 5.00 % |
ASTM D790 |
Arkema Group KYNAR® 1000 HD Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili.. |
|||
Flexural Strength | 58.0 - 76.0 MPa @Strain 5.00 % |
8410 - 11000 psi @Strain 5.00 % |
ASTM D790 |
Arkema Group KYNAR® 760 Polyvinylidene Fluoride Homopolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili.. |
|||
Flexural Strength | <= 58.0 MPa | <= 8410 psi | ISO 178 |
Polykemi AB POLYfill PPH T20040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | <= 58.0 MPa | <= 8410 psi | ISO 178 |
Polykemi AB POLYfill PPH T5040 FC Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | <= 58.0 MPa | <= 8410 psi | ISO 178 |
Polykemi AB POLYfill PPH T5040DS Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant Information provided by Polykemi AB |
|||
Flexural Strength | <= 58.0 MPa | <= 8410 psi | ISO 178 |
Polykemi AB POLYfill PPH T5040 FC VT Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |