Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Creep Strength | 827 MPa @Temperature 260 °C, Time 36000 sec |
120000 psi @Temperature 500 °F, Time 10.0 hour |
|
ATI Allegheny Ludlum AL 13-8™ H 1100 Precipitation Hardening Alloy Characteristics: excellent strength, high hardness, superior toughness, good corrosion resistance, good transverse toughness properties, strength and ductility can be tailored by varying the aging t.. |
|||
Creep Strength | 827 MPa @Temperature 260 °C, Time 36000 sec |
120000 psi @Temperature 500 °F, Time 10.0 hour |
|
ATI Allegheny Ludlum AL 13-8™ H 950 Precipitation Hardening Alloy Characteristics: excellent strength, high hardness, superior toughness, good corrosion resistance, good transverse toughness properties, strength and ductility can be tailored by varying the aging t.. |
|||
Creep Strength | 827 MPa @Temperature 260 °C, Time 36000 sec |
120000 psi @Temperature 500 °F, Time 10.0 hour |
|
ATI Allegheny Ludlum AL 13-8™ H 1000 Precipitation Hardening Alloy Characteristics: excellent strength, high hardness, superior toughness, good corrosion resistance, good transverse toughness properties, strength and ductility can be tailored by varying the aging t.. |
|||
Creep Strength | 827 MPa @Temperature 260 °C, Time 36000 sec |
120000 psi @Temperature 500 °F, Time 10.0 hour |
|
ATI Allegheny Ludlum AL 13-8™ H 1025 Precipitation Hardening Alloy Characteristics: excellent strength, high hardness, superior toughness, good corrosion resistance, good transverse toughness properties, strength and ductility can be tailored by varying the aging t.. |
|||
Creep Strength | 827 MPa @Temperature 260 °C, Time 36000 sec |
120000 psi @Temperature 500 °F, Time 10.0 hour |
|
ATI Allegheny Ludlum AL 13-8™ H 1050 Precipitation Hardening Alloy, Heat Treated at 1050°F Characteristics: excellent strength, high hardness, superior toughness, good corrosion resistance, good transverse toughness properties, strength and ductility can be tailored by varying the aging t.. |
|||
Creep Strength | 827 MPa @Temperature 260 °C, Time 36000 sec |
120000 psi @Temperature 500 °F, Time 10.0 hour |
|
ATI Allegheny Ludlum AL 13-8™ H 1050 Precipitation Hardening Alloy, Heat Treated at 1150°F Characteristics: excellent strength, high hardness, superior toughness, good corrosion resistance, good transverse toughness properties, strength and ductility can be tailored by varying the aging t.. |