Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Creep Strength | 100 MPa @Temperature 1200 °C, Time >=360000 sec |
14500 psi @Temperature 2190 °F, Time >=100 hour |
|
COI Ceramics Nextel™ A-N720 Oxide Ceramic Matrix Composite, Alumina Description: Oxide ceramic matrix composites products are based upon sol-gel derived matrices and 3M Corporation's Nextel™ fiber products. These materials can be used up to 1200ºC (2200ºF) in air.. |
|||
Creep Strength | 100 MPa @Strain 0.650 %, Time 3600 sec |
14500 psi @Strain 0.650 %, Time 1.00 hour |
|
Akro-Plastic Akroloy® PA GF 50 (2706) PA 6.6 & PA6I/6T Dry, 50% Glass Filled One of the most characteristic properties of polyamide (PA 6.6) is the absorption of moisture. This essentially leads to increased toughness and elongation at break, to name the most important param.. |
|||
Creep Strength | 100 MPa @Strain 0.700 %, Time 36000 sec |
14500 psi @Strain 0.700 %, Time 10.0 hour |
|
Akro-Plastic Akroloy® PA GF 50 (2706) PA 6.6 & PA6I/6T Dry, 50% Glass Filled One of the most characteristic properties of polyamide (PA 6.6) is the absorption of moisture. This essentially leads to increased toughness and elongation at break, to name the most important param.. |
|||
Creep Strength | 100 MPa @Strain 0.800 %, Time 360000 sec |
14500 psi @Strain 0.800 %, Time 100 hour |
|
Akro-Plastic Akroloy® PA GF 50 (2706) PA 6.6 & PA6I/6T Dry, 50% Glass Filled One of the most characteristic properties of polyamide (PA 6.6) is the absorption of moisture. This essentially leads to increased toughness and elongation at break, to name the most important param.. |
|||
Creep Strength | 100 MPa @Strain 0.880 %, Time 3.60e+6 sec |
14500 psi @Strain 0.880 %, Time 1000 hour |
|
Akro-Plastic Akroloy® PA GF 50 (2706) PA 6.6 & PA6I/6T Dry, 50% Glass Filled One of the most characteristic properties of polyamide (PA 6.6) is the absorption of moisture. This essentially leads to increased toughness and elongation at break, to name the most important param.. |
|||
Creep Strength | 100 MPa @Strain 0.550 %, Time 3600 sec |
14500 psi @Strain 0.550 %, Time 1.00 hour |
|
Akro-Plastic Akromid® T1 GF 50 (3101) PPA Dry, 50% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high.. |
|||
Creep Strength | 100 MPa @Strain 0.580 %, Time 36000 sec |
14500 psi @Strain 0.580 %, Time 10.0 hour |
|
Akro-Plastic Akromid® T1 GF 50 (3101) PPA Dry, 50% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high.. |
|||
Creep Strength | 100 MPa @Strain 0.600 %, Time 360000 sec |
14500 psi @Strain 0.600 %, Time 100 hour |
|
Akro-Plastic Akromid® T1 GF 50 (3101) PPA Dry, 50% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high.. |
|||
Creep Strength | 100 MPa @Strain 0.650 %, Time 3.60e+6 sec |
14500 psi @Strain 0.650 %, Time 1000 hour |
|
Akro-Plastic Akromid® T1 GF 50 (3101) PPA Dry, 50% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high.. |