Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 1.91 MPa | 277 psi | 72 hrs at standard temperature in AMS 3021 |
3M AC-370 Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-370 Class B are fast cure, low density polysulfide sealants suitable for fuel tank and fuselage applications. These two-component, manganese dioxide cured sealants are solven.. |
|||
Tensile Strength at Break | 1.91 MPa | 277 psi | 72 hrs at standard temperature in AMS 3020 |
3M AC-370 Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-370 Class B are fast cure, low density polysulfide sealants suitable for fuel tank and fuselage applications. These two-component, manganese dioxide cured sealants are solven.. |
|||
Tensile Strength at Break | 1.91 MPa | 277 psi | 72 hrs at standard temperature in AMS 3021 |
3M AC-370 Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-370 Class B are fast cure, low density polysulfide sealants suitable for fuel tank and fuselage applications. These two-component, manganese dioxide cured sealants are solven.. |
|||
Tensile Strength at Break | 1.91 MPa | 277 psi | 72 hrs at standard temperature in AMS 3020 |
3M AC-370 Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-370 Class B are fast cure, low density polysulfide sealants suitable for fuel tank and fuselage applications. These two-component, manganese dioxide cured sealants are solven.. |