Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 103 MPa | 14900 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne LubriOne™ NI-20GF/15T FR Polyamide 610 (Nylon 610) Information provided by PolyOne |
|||
Tensile Strength at Break | 103 MPa | 14900 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ GMF 600 A 40 Storm Grey Polyamide 6 (Nylon 6) The Nymax® GMF 600 Series of compounds are based upon nylon 6 resins and select combinations of glass fiber and mineral reinforcements offering a unique balance of physical property and part perfor.. |
|||
Tensile Strength at Break | 103 MPa | 15000 psi | ASTM D638 |
Polymer Resources PEI-GP1 Polyetherimide, Flame Retardant Polyetherimide, Flame Retardant, High Heat ResistanceProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information.. |
|||
Tensile Strength at Break | 103 MPa | 15000 psi | ASTM D638 |
Polymer Resources PPX-G30 Modified-PPO, 30% Glass Reinforced Modified-Polyphenylene Oxide, 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
Tensile Strength at Break | 103 MPa | 15000 psi | ASTM D638 |
Ravago Manufacturing Americas Hylon® N1033THL Nylon 6/6 (Cond) Information provided by Ravago. |
|||
Tensile Strength at Break | 103 MPa | 14900 psi | ISO 527-2 |
Ravago Manufacturing Americas Hylon® N1213HL BK Nylon 6/6 Available in North America Filler: Glass Fiber Reinforcement, 13% Filler by WeightAdditive: Heat Stabilizer and Lubricant Features: Lubricated and Heat StabilizedRoHS CompliantForm: Pellets Proces.. |
|||
Tensile Strength at Break | 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 2312 PEI 30% Milled glass filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. |
|||
Tensile Strength at Break | 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® K4530 PBT (Europe-Africa-Middle East) 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors. |
|||
Tensile Strength at Break | 103 MPa | 14900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® SHF434HR PBT PBT, Super High Flow, 20% glass reinforced,hydrolytically resistant. |
|||
Tensile Strength at Break | 103 MPa | 14900 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DF0049 PC LNP THERMOCOMP* DF0049 is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Flame Retardant. |
|||
Tensile Strength at Break | 103 MPa | 14900 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DF004E PC LNP THERMOCOMP* DF004E is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding. |
|||
Tensile Strength at Break | 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RF003H PA 66 LNP* THERMOCOMP* RF003H is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
Tensile Strength at Break | 103 MPa | 14900 psi | ASTM D638 |
SABIC Innovative Plastics LNP VERTON MV006S PP (Europe-Africa-Middle East) LNP VERTON* MV006S is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. |
|||
Tensile Strength at Break | 103 MPa | 15000 psi | ASTM D638 |
A. Schulman SCHULADUR® B GF15 15% Glass Fiber Reinforced PET Information provided by A. Schulman. |
|||
Tensile Strength at Break | 103 MPa | 14900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP GF004 PSU (Europe-Africa-Middle East) LNP* Thermocomp* GF004 is a compound based on Polysulfone resin containing Glass Fiber. |