Polymer Property : Tensile Strength at Break = 11.25 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	<= 11.25 MPa	<= 1632 psi	after aging (240h, 135°C); IEC 60811-1-2
Borealis Visico™/Ambicat™ LE4421/LE4472 Polyethylene Compound, Crosslinkable Visico™ LE4421 / Ambicat™ LE4472 is a silane crosslinkable black compound designed for covering/insulation of overhead cables. The base material Visico™ LE4421 in combination with the catalyst m..
Tensile Strength at Break	<= 11.25 MPa	<= 1632 psi	after aging (240h, 135°C); IEC 60811-1-2
Borealis Visico™/Visico™ LE4421/LE4438 Polyethylene Compound, Crosslinkable Visico™ LE4421 / Visico™ LE4438 is a silane crosslinkable natural compound designed for low voltage power cables up to 6 kV. Visico™ LE4421 and Visico™ LE4438 is a combination of a Visico™ bas..
Tensile Strength at Break	<= 11.25 MPa	<= 1632 psi	after aging (240h, 135°C); IEC 60811-1-2
Borealis Visico™/Visico™ LE4421M/LE4431M Polyethylene Visico™ LE4421M / Visico™ LE4431M is a two-part silane crosslinkable insulation system, specially designed for insulation applications. Applications: Visico™ LE4421M / Visico™ LE4431M is intend..
Tensile Strength at Break	<= 11.25 MPa	<= 1632 psi	after aging (240h, 135°C); IEC 60811-1-2
Borealis Visico™/Visico™ LE4423/LE4438 Polyethylene Compound, Crosslinkable Visico™ LE4423 / Visico™ LE4438 is a silane crosslinkable natural compound designed for low voltage power cables up to 6 kV. Visico™ LE4423 and Visico™ LE4438 is a combination of a Visico™ bas..
Tensile Strength at Break	<= 11.25 MPa	<= 1632 psi	after aging (240h, 135°C); IEC 60811-1-2
Borealis Visico™/Ambicat™ LE4427/LE4476 Polyethylene Compound, Crosslinkable Visico™ LE4427 / Ambicat™ LE4476 is a silane crosslinkable black compound designed for weather resistant covering/insulation of overhead and façade cables. The black base material Visico™ LE442..
Tensile Strength at Break	11.25 MPa	1632 psi	ASTM D638
Bayshore Vinyl Compounds BVC 6200-65 Vinyl Compound BVC 6200-65 is an economy grade flexible vinyl formulation designed for easy processing and excellent heat stability. This material will process at high rates with low temperatures and produces a s..
Tensile Strength at Break	<= 11.25 MPa	<= 1632 psi	after aging (240h, 135°C, 5% catalyst); IEC 60811-1-2
Borealis Visico™/Ambicat™ LE4421/LE4476 Polyethylene Compound, Crosslinkable Visico™ LE4421 / Ambicat™ LE4476 is a silane crosslinkable natural compound designed for low voltage power cables up to 6kV. The base material Visico™ LE4421 in combination with the catalyst mas..