Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 145 MPa | 21000 psi | |
Plastcom SLOVAMID 6 GF 25 FRG 5 PA6, 25% glass fibre, flame retardant FeaturesPA 6 for injection moulding, chemically reinforced with 25% glass fibre, with nonhalogen flame retardant. Main features: flammability in accordance with UL 94 V0 at 1.6 mm, glow wire at 960°.. |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ ND633 GF Black Polyamide 6 (Nylon 6) The Nymax® GF 600 Series of glass fiber-reinforced nylon 6 compounds have been specifically engineered for applications requiring high stiffness, tensile strength, and toughness, while providing en.. |
|||
Tensile Strength at Break | <= 145 MPa | <= 21000 psi | ISO/R527 |
Polykemi AB POLYshine PBT D311 GF30 PBT, Glass-Fiber Reinforced, Modified Information provided by Polykemi AB |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DFL28 PC LNP* Lubricomp* DFL28 is a compound based on Polycarbonate resin containing 40% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated. |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DFL28 PC (Asia Pacific) LNP* Lubricomp* DFL28 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527-1/-2 |
DSM Arnite® TV4 460 KL TV4 460 PBT/PET Blend-30% Glass Reinforced (European Grade)
(discontinued **) Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame .. |
|||
Tensile Strength at Break | <= 145 MPa | <= 21000 psi | ISO/R527 |
Polykemi AB POLYshine PBT D204 GF30 FR PBT, Glass Fiber Reinforced, Flame Retardant Information provided by Polykemi AB |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527-1, -2; 5 mm/min |
Lanxess Pocan® ECO T 3230 000000 PBT + PET, 30% Glass Fiber PBT + PET, 30% glass fibers, injection molding, improved surface finish, contains 30% post-consumer recycled material, increased temperature peak loadInformation provided by LANXESS. |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | cond.; ISO 527-1, -2; 5 mm/min |
Lanxess Durethan® AKV 40 H2.0 901510 Nylon 66, Glass Fiber Reinforced PA 66, 40% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS. |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RFL25ES PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFL25ES is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Easy Molding. |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP JCL36E PES LNP* LUBRICOMP* JCL36E is a compound based on Polyethersulfone (PES) resin containing 30% Carbon Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® V8280 PBT+PET (Europe-Africa-Middle East) 40% GR PBT+PET. High stiffness. Excellent surface aesthetics. Applications include office furniture. |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | ASTM D638 |
A. Schulman SCHULADUR® B GF30 30% Glass Fiber Reinforced PET Information provided by A. Schulman. |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527-93 |
Wellman Wellamid® GF33-66/6 XE-BK167A 33% Glass Filled, Color Matched Ebony Nylon 66/6 Description: Glass Filled, Color Matched Ebony Nylon 66/6Information provided by Wellman. |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® XE 4104 nat PA610-GF40 Product description: Grilamid XE 4104 natural is a 40% glass fiber reinforced, heat stabilized polyamide 610 injection molding grade. This product is to a large extent based on renewable raw materia.. |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527-1/-2 |
DuPont Performance Polymers Crastin® SK609 BK851 Polybutylene Terephthalate (PBT)
(Unverified Data**) 50% Glass Reinforced Polybutylene Terephthalate Crastin SK609 BK851 is a 50% glass fiber reinforced lubricated black polybutylene terephthalate resin for injection molding.Information provided by Du.. |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527-1/-2 |
DuPont Performance Polymers Delrin® 525GR NC000 Acetal (POM)
(Unverified Data**) 25% Glass Reinforced Medium Viscosity Acetal Homopolymer Delrin 525GR NC000 is a 25% glass reinforced acetal homopolymer for injection molding. It has very high strength stiffness and high deflectio.. |
|||
Tensile Strength at Break | 145 MPa @Temperature 22.8 °C |
21000 psi @Temperature 73.0 °F |
ASTM D638 |
Ensinger TECATOR™ TI 5013 Polyamide-imide (PAI) TECATOR™ is a high performance melt processable polyamideimide that maintains its excellent mechanical and wear properties in temperature environments exceeding 500°F. Stock shapes from Ensinger .. |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® GV-2 FWA black 9225 PA*-GF20 Product description: Grivory GV-2 FWA black 9225 is a 20% glass fiber reinforced engineering thermoplastic material based on a combination of semicrystalline polyamide with partially aromatic copoly.. |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527 |
Eurostar Starflam PF0057E PA6, 25% Glass Filled, Injection Molded Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Fiber Reinforced, Polyamide 6 Injection Molding Resin (also known as PF-1005 Z270)Information provided by Polymer Technology & Services,.. |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527 |
Eurotec® Tecomid® MB40 GR20 NL PA6, 20% glass fiber reinforced, natural Information provided by Eurotec® |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527-1 |
Barlog Plastics KEBATRON L2040G3 PPS, linear, 40% glass fiber reinforced, reduced residual chlorine PPS-GF40Information provided by BARLOG plastics GmbH. |
|||
Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R533H BK0201 Nylon 66, 33% Glass Reinforced, Conditioned Vydyne® R533H BK0201 is 33% glass-fiber reinforced, hydrolysis-resistant, heat-stabilized PA66 resin. Available in black, it is specifically designed to maximize the retention of physical propertie.. |