Polymer Property : Tensile Strength at Break = 16.3 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	16.3 MPa	2370 psi	2 in/min; ASTM D638
Ineos N01G-02 Polypropylene Impact Copolymer N01G-02 is a low melt flow rate polypropylene impact copolymer designed for blow molding, extrusion, and compounding applications. The grade benefits from a very high impact resistance at room and l..
Tensile Strength at Break	16.3 MPa	2360 psi	ASTM D412
UBE UBEPOL BR150B Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 35 Minutes at 145°C) Description: UBEPOL BR is UBE's line of polybutadiene rubber products.Information provided by UBE.
Tensile Strength at Break	16.3 MPa	2360 psi	ASTM D412
Compuestos Dominicanos Polycom AK-050380 PVC Description: Compuestos Dominicanos, S.A. manufactures PVC compounds for the production of high quality electrical wire and cable with excellent insulation properties and smooth finish. Polycom prod..
Tensile Strength at Break	16.3 MPa	2360 psi	ASTM D412
Compuestos Dominicanos Polycom AK-051090 PVC Compound Compuestos Dominicanos, S.A. manufactures high quality covering PVC for the production of electrical wire and cable providing excellent insulation properties and smooth finish. Their products are d..
Tensile Strength at Break	16.3 MPa	2370 psi	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
3M Dyneon™ FE 5640Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5640Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu..
Tensile Strength at Break	16.3 MPa	2360 psi	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
3M Dyneon™ FG 5690Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FG 5690Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu..
Tensile Strength at Break	16.3 MPa	2370 psi	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
3M Dyneon™ FC 2180 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2180 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul..