Polymer Property : Tensile Strength at Break = 2.41 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 2.41 MPa
350 psi
Reinforced Material - Fill; ASTM D412
Parker Chomerics CHO-SEAL 1285R Reinforced Conductive Elastomer Seal
These materials are fabric-reinforced, silver-plated-aluminum filled EMI seals for airframe shielding applications. These seal materials can also be used to maintain surface electrical continuity at..
Tensile Strength at Break 2.41 MPa
350 psi
Reinforced Material - Fill; ASTM D412
Parker Chomerics CHO-SEAL 1287R Reinforced Conductive Elastomer Seal
These materials are fabric-reinforced, silver-plated-aluminum filled EMI seals for airframe shielding applications. These seal materials can also be used to maintain surface electrical continuity at..
Tensile Strength at Break 2.41 MPa
350 psi
Zircar Zirconia Buster M-35 Alumina Board, Disc, and Cylinder Insulation
Zircar alumina insulation Type Buster is a rigid, fibrous ceramic material produced by vacuum forming alumina fibers with either a high purity alumina binder in BusterA-30 for use at 1600C or with s..
Tensile Strength at Break 2.41 MPa
350 psi
ASTM D412
Teknor Apex Monprene® MP-2238-R Thermoplastic Elastomer
Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo..
Tensile Strength at Break 2.41 MPa
350 psi
ASTM D412
Teknor Apex Monprene® MP-2315 Thermoplastic Elastomer
Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo..
Tensile Strength at Break 2.41 MPa
350 psi
ASTM D412
Teknor Apex Monprene® MP 1672 Thermoplastic Elastomer
Features: Monprene® TPE gels are softer than the shore A range of hardness. Monprene® TPE gels are high strength and high flow elastomers that may be used in the overmolding processes on poly..
Tensile Strength at Break 2.41 MPa
350 psi
Zircar Zirconia Buster M-35 Alumina Board, Disc, and Cylinder Insulation
Zircar alumina insulation Type Buster is a rigid, fibrous ceramic material produced by vacuum forming alumina fibers with either a high purity alumina binder in BusterA-30 for use at 1600C or with s..
Tensile Strength at Break 2.41 MPa
350 psi
Standard Cure - 14 days
3M AC-236 Class B-1/2 Aerospace Sealant
3M Aerospace Sealant AC-236 Class B are two-component, manganese dioxide cured, liquid polysulfide polymer system providing excellent fuel tank and fuselage seals. They have outstanding resistance t..
Tensile Strength at Break 2.41 MPa
350 psi
Standard Cure - 14 days
3M AC-236 Class B-2 Aerospace Sealant
3M Aerospace Sealant AC-236 Class B are two-component, manganese dioxide cured, liquid polysulfide polymer system providing excellent fuel tank and fuselage seals. They have outstanding resistance t..
Tensile Strength at Break 2.41 MPa

@Time 1.21e+6 sec
350 psi

@Time 336 hour
Standard Cure
3M AC-251 Black Class B-1 Aerospace Sealant
3M Aerospace Sealant AC-251 Black Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate ai..
Tensile Strength at Break 2.41 MPa

@Time 1.21e+6 sec
350 psi

@Time 336 hour
Standard Cure
3M AC-251 Black Class B-1/2 Aerospace Sealant
3M Aerospace Sealant AC-251 Black Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate ai..
Tensile Strength at Break 2.41 MPa

@Time 1.21e+6 sec
350 psi

@Time 336 hour
Standard Cure
3M AC-251 Black Class B-2 Aerospace Sealant
3M Aerospace Sealant AC-251 Black Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate ai..
Tensile Strength at Break 2.41 MPa

@Time 1.21e+6 sec
350 psi

@Time 336 hour
Standard Cure
3M AC-251 Gray Class B-1/2 Aerospace Sealant
3M Aerospace Sealant AC-251 Gray Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate air..
Tensile Strength at Break 2.41 MPa

@Time 1.21e+6 sec
350 psi

@Time 336 hour
Standard Cure
3M AC-251 Gray Class B-2 Aerospace Sealant
3M Aerospace Sealant AC-251 Gray Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate air..
Tensile Strength at Break 2.41 MPa
350 psi
Standard Cure - 14 days; AMS3276
3M AC-275 Class B-1/2 Aerospace Sealant
3M Aerospace Sealant AC-275 Class B is a high temperature two-component manganese dioxide cured, liquid polysulfide polymer sealants providing excellent fuel tank and fuselage seals. They have outst..
Tensile Strength at Break 2.41 MPa
350 psi
Standard Cure - 14 days; AMS3276
3M AC-275 Class B-2 Aerospace Sealant
3M Aerospace Sealant AC-275 Class B is a high temperature two-component manganese dioxide cured, liquid polysulfide polymer sealants providing excellent fuel tank and fuselage seals. They have outst..
Tensile Strength at Break 2.41 MPa
350 psi
Standard Cure - 14 days; AMS3276
3M AC-275 Class B-4 Aerospace Sealant
3M Aerospace Sealant AC-275 Class B is a high temperature two-component manganese dioxide cured, liquid polysulfide polymer sealants providing excellent fuel tank and fuselage seals. They have outst..
Tensile Strength at Break 2.41 MPa
350 psi
Standard Heat Cycle +JRF - 7 days @ 60°C
3M AC-350 Class A-1 Aerospace Sealant
3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have..
Tensile Strength at Break 2.41 MPa

@Temperature 182 °C,
Time 28800 sec
350 psi

@Temperature 360 °F,
Time 8.00 hour
3M AC-350 Class A-1 Aerospace Sealant
3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have..
Tensile Strength at Break 2.41 MPa
350 psi
Standard Heat Cycle +JRF - 7 days @ 60°C
3M AC-350 Class A-1/2 Aerospace Sealant
3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have..
Tensile Strength at Break 2.41 MPa

@Temperature 182 °C,
Time 28800 sec
350 psi

@Temperature 360 °F,
Time 8.00 hour
3M AC-350 Class A-1/2 Aerospace Sealant
3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have..
Tensile Strength at Break 2.41 MPa
350 psi
Standard Heat Cycle +JRF - 7 days @ 60°C
3M AC-350 Class A-2 Aerospace Sealant
3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have..
Tensile Strength at Break 2.41 MPa

@Temperature 182 °C,
Time 28800 sec
350 psi

@Temperature 360 °F,
Time 8.00 hour
3M AC-350 Class A-2 Aerospace Sealant
3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have..
Tensile Strength at Break 2.41 MPa
350 psi
ASTM D 412
RTP Company RTP 2800 B-55A FR Thermoplastic Vulcanizate Elastomer (TPV), Flame Retardant  (discontinued **)<
Data for this product has not been recently verified, please contact RTP Company for more information before specifying this grade.
Tensile Strength at Break 2.41 MPa
350 psi
Standard Cure - 14 days
3M AC-236 Class B-4 Aerospace Sealant
3M Aerospace Sealant AC-236 Class B are two-component, manganese dioxide cured, liquid polysulfide polymer system providing excellent fuel tank and fuselage seals. They have outstanding resistance t..