Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 14.8 MPa | 2140 psi | ASTM D638 |
Teknor Apex APEX® 3707-70LG-NT Polyvinyl Chloride, Flexible Notes: RoHS Compliant Uses: Medical/Healthcare Applications Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 14.8 MPa | 2140 psi | ASTM D412 |
Teknor Apex Telcar® TL-86-K902A Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | 14.8 MPa | 2140 psi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FG 5630Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FG 5630Q can be compounded using standard water cooled internal mixers or two-roll mills. The “dry” ingredients should be blended before adding to the masticated gum... |
|||
Tensile Strength at Break | 14.8 MPa | 2140 psi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FC 2120 Fluoroelastomer 3M™ Dyneon™ Flouroelastomer FC 2120 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |