- Polymer Property : Tensile Strength at Break = 33.0 MPa
Polymer Property : Tensile Strength at Break = 33.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycolac® MG34LG ABS Automotive: Low gloss ABS for unpainted interior applications. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycolac® MG38F ABS (Asia Pacific) Very high impact ABS. Toughness/rigidity. FDA compliant. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycolac® MG47 ABS (Europe-Africa-Middle East) Multi-purpose, injection molding ABS providing a favorable balance of engineering properties. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics GELOY CR8510 ASA (Asia Pacific) ASA with outstanding UV exposure performance for both exterior and interior applications. F1 Rated. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO 527 |
| Total Evatane® 28 - 03 HDPE, blown film
(discontinued **) EVA Copolymer made by high pressure tubular process. Temperature profile (°C) for injection molding: 130 to 160.Information provided provided by Total Petrochemicals.Total Petrochemicals includes f.. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ASTM D638 |
| Braskem BS 002 HDPE Blow Molding Polyethylene
(discontinued **) Applications: Bottles for medicines, cleaning products, cosmetics, food products and surface-active agents. Information provided by Braskem |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO R 527 |
| Fainplast Compounds RK 320 Rigid PVC, Extrusion Lead Free Indoor profiles |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO 37 |
| Huntsman AVALON® 95 AE Thermoplastic Polyurethane Introduction: AVALON 95 AE is a general purpose polyester based thermoplastic polyurethane for injection molding. AVALON 95 AE is part of the AVALON Perform Range and offers a premium soiling materi.. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO 527 |
| GEHR Plastics ECOGEHR® PLA-LF Polylactic Acid PLA-L is a blend of polylactide, lignin, lingo-cellulosic, natural fatty acids, waxes and wood fibers. This material possesses good mechanical properties similar to ABS. This bioplastic has an opera.. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP DZL34E PC LNP* Lubricomp* DZL34E is a compound based on Polycarbonate resin containing 20% Milled Glass, 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP DZL34E PC (Asia Pacific) LNP* Lubricomp* DZL34E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP DZL34E PC (Asia Pacific) LNP* Lubricomp* DZL34E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | UL 1581 |
| SABIC Innovative Plastics NORYL WCA105 PPE-TPE Flexible, non-halogenated FR mPPE extrusion grade ideal for evaluation in applications such as wire insulation. Flame retardant performance capable of meeting VW1 and 105C temperature rating requir.. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP MX06404 PP LNP LUBRICOMP* MX06404 is a compound based on Polypropylene resin containing 20% Glass Fiber and 15% PTFE. Added features of this material include: Heat Stabilized, Low Extractable, Wear Resistant... |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-LOY A30009 ABS (Europe-Africa-Middle East) LNP* Stat-Loy* A30009 is a compound based on Acrylonitrile Butadiene resin, containing Proprietary Filler, Flame Retardant. Added features include : Permanent Antistatic, Flame retardant. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ASTM D638 |
| SCG Chemicals EL-Leneâ„¢ H511W High Density Polyethylene Wire & Cable Grade Key Characteristics: Contains special metal deactivator, high mechanical properties, high speed extrusionRecommended Applications: Insulation of communication cablesInformation provided by SCG Che.. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Crosshead speed 100 mm/min; ISO 527 |
| SCG Chemicals EL-Leneâ„¢ H5211PC High Density Polyethylene Pipe Resin Key Characteristics: Good processing, high thermal stability, good balance of MRS, SCG, and RCPRecommended Applications: Water pressure and gas pipesCertification: Certified by EXOVA, LNE, AENOR,.. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | 50mm/min; ISO 527-2 |
| Borealis Borcell™ HE1123 High Density Polyethylene Borcell™ HE1123 is a high density polyethylene compound intended for the insulation of radio frequency coaxial cables. Borcell™ HE1123 is designed to give the lowest possible cable attenuation by.. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | |
| UBE C (Low-Cis) HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %) Description: UBE high impact polystyrene (HIPS).Information provided by UBE. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO 527-3/5/500 |
| Lubrizol Estane® 54643 Polyester-Based Thermoplastic Polyurethane Feature: Excellent flame retardant properties, matt surface appearance and low surface friction and transparent spherical pelletsUses: Melt roll coated fabrics and calenderingAvailable in Americas, .. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO 527-1/-2 |
| Covestro Desmopan® W DP89085A Polyurethane PreprocessingMax. Water content |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | 50 mm/min; ISO 527 |
| Chi Mei Polylac® PA-758R ABS - Transparent Transparent, Chemical Resistant |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO R 527 |
| Fainplast Compounds MRT 168 Medical Rigid PVC, Injection Molding Anti impact connectors |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO R 527 |
| Addiplast Addilene H 140 Polypropylene Homopolymer Unreinforced, low flow for injection and extrusion, very translucentInformation provided by Addiplast. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ASTM D412 |
| Alliance Polymers Zythane™ 5080A Thermoplastic Polyurethane Elastomer Zythane™ 5080A is a polycaprolactone-based TPU specifically formulated for injection molding applications .It exhibits excellent low compression set, abrasion resistance and toughness and has good .. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ASTM D638 |
| Aclo Accucomp ABS ABS803L Medium Impact Grade |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics GELOY CR7500 ASA (Asia Pacific) High heat ASA with optimum flow-impact balance. For Automotive applications and Automotive colors only. |
|||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO R 527 |
| Fainplast Compounds RE 130 Rigid PVC, Extrusion Pipes and profiles |
|||