Polymer Property : Tensile Strength at Break = 33800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	233 MPa	33800 psi	ISO 527
SABIC Innovative Plastics LNP STAT-KON RE004 PA 66 LNP* STAT-KON* RE004 is a compound based on Nylon 66 resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break	233 MPa	33800 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PX12419 PA 6 LNP* THERMOCOMP* PX12419 is a compound based on Nylon 6 containing Carbon Fiber. Added features of this grade include: Electrically Conductive.
Tensile Strength at Break	233 MPa	33800 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP QC008 PA6.10 LNP* THERMOCOMP* QC008 is a compound based on Nylon 6/10 containing 40% Carbon Fiber. Added feature of this grade is: Electrically Conductive.
Tensile Strength at Break	233 MPa	33800 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Verton PV00A PA 6 (Europe-Africa-Middle East) LNP* Verton* PV00A is a compound based on Nylon 6 resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength at Break	233 MPa	33800 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® 73G50HSLA BK416 Nylon 6 (Unverified Data**) 50% Glass Reinforced Heat Stabilized Polyamide 6 Zytel 73G50HSLA BK416 is a 50% glass fiber reinforced heat stabilized lubricated polyamide 6 resin for injection molding. It has an excellent surface..