Polymer Property : Tensile Strength at Break = 3390 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	23.4 MPa	3390 psi	Type IV, 51 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable W84592L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength at Break	23.4 MPa	3390 psi	Type I, 51 mm/min; ASTM D638
PolyOne Trilliant™ HC X THC 1101 Natural Copolyester Trilliant™ HC high performance blends offer outstanding strength, durability and chemical resistance through the combination of Eastman Tritan™ copolyester with other various polymeric resins. Tri..
Tensile Strength at Break	23.4 MPa	3390 psi	Type I, 51 mm/min; ASTM D638
PolyOne Edgetek® XT X XT 1001 Natural Copolyester Edgetek™ XT high performance blends offer outstanding strength, durability and chemical resistance through the combination of Eastman Tritan™ copolyester with other various polymeric resins. Edget..
Tensile Strength at Break	23.4 MPa	3390 psi	ASTM D638
Resirene Resirene® 2270 High Impact Polystyrene Features:Medium FlowGood GlossFDA Rating: 21 CFR 177.1640High ProductivityApplications:Extrusion/ ThermoformingInjectionDiskettesPen BarrelsInformation provided by US distributor Calsak Corporation...
Tensile Strength at Break	23.4 MPa	3390 psi	ASTM D4894
3M Dyneon™ CC174-N PTFE, 15% Fiberglass/Moly Filled (discontinued **) Product Form: Gray, non-pelletized powder. Applications include bearings, rider rings, and packings.Data provided by Dyneon.
Tensile Strength at Break	23.4 MPa	3390 psi	chs 2.0 in/min; ASTM D638
Diamond Polymers Centrex® 601 Profile Extrusion Grade AES Centrex 601 resin is a very high-impact, low-gloss AES (acrylonitrile-ethylene-propylene-styrene) resin with good resistance to weather aging. It has good melt strength for profile extrusion and can..
Tensile Strength at Break	23.4 MPa	3390 psi	chs 0.2 in/min; ASTM D638
Diamond Polymers Centrex® 835 Sheet Extrusion Grade Centrex 835 resin is a low-gloss grade of ASA (acrylonitrile-styrene-acrylate) with good resistance to weather aging. It has good melt strength for extrusion and thermoforming applications. Centrex ..
Tensile Strength at Break	23.4 MPa @Temperature 23.0 °C	3390 psi @Temperature 73.4 °F	ASTM D638, ISO 527-2
DuPont™ Surlyn® 6320 Magnesium Ionomer Surlyn® 6320 is a magnesium ionomer thermoplastic resin. It is available for use in conventional extrusion and injection equipment, to create various sheets or shapes. Surlyn® 6320 thermoplastic r..
Tensile Strength at Break	23.4 MPa	3390 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Syncure™ S1075A Polyethylene, Crosslinked (XLPE) Moisture Crosslinkable Polyethylene Compound. Available as Base Resin component for PolyOne Syncure System.Tensile, Elongation, Deformation, Hot Creep, and Gel measured on a 95 phr S1074A / 5 phr S1..