Polymer Property : Tensile Strength at Break = 39.2 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	39.2 MPa	5690 psi	ASTM D638
Samsung Cheil Industries Starex® VH-0850 ABS, Unreinforced (discontinued **) Amorphous Acrylonitrile Butadiene Styrene (ABS)Characteristics: Flame Retardant: Balance of Properties (Impact, Mechanical and Heat)Applications: Computer, Monitor and Printer Housings, Microwave Co..
Tensile Strength at Break	39.2 MPa	5690 psi	ASTM D412
Huntsman IROGRANÂ® PS 455-215 TPU-Polyester Polyester-based grades with a broad processing window ideally suited for cast, flat die and flown film lines.Information provided by Alliance Polymers
Tensile Strength at Break	39.2 MPa @Thickness 2.00 mm	5690 psi @Thickness 0.0787 in	50mm/min; ASTM D638
LG Chemical KEYFLEX BT HB9255D Ester Type TPE Description: TPC-ET, Blow Moldable, Medium Modulus, Black ColorApplication: Air duct, Hose & TubingCAS: 37282-12-5, 24968-12-5 and 1333-86-4Information provided by LG Chemical
Tensile Strength at Break	39.2 MPa	5690 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® HG-0760LT ABS, Unreinforced Information provided by Samsung Cheil Industries.
Tensile Strength at Break	39.2 MPa	5690 psi	ASTM D638
Samsung Cheil Industries StarexÂ® SF-0505H MABS, Unreinforced Scratch Resistant Information provided by Samsung Cheil Industries.
Tensile Strength at Break	39.2 MPa	5690 psi	50 mm/min; ASTM D638
Samsung Cheil Industries InfinoÂ® WP-1041G PC/ABS, Unreinforced Metal Plating Grade Information provided by Samsung Cheil Industries.
Tensile Strength at Break	39.2 MPa	5690 psi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® HG-0760LT ABS, Unreinforced Information provided by Samsung Cheil Industries.
Tensile Strength at Break	39.2 MPa	5690 psi	ASTM D638
Samsung Cheil Industries StarexÂ® SF-0505H MABS, Unreinforced Scratch Resistant Information provided by Samsung Cheil Industries.
Tensile Strength at Break	39.2 MPa	5690 psi	50 mm/min; ASTM D638
Supreme Petrochem SP 255 Toughened Polystyrene Characteristics Superior flexibility Excellent flow grade High ball drop strength Good clarityProcessing Extrusion Thermoforming Injection MoldingApplications Transparent hangers, stationery it..
Tensile Strength at Break	39.2 MPa	5690 psi	50 mm/min; ASTM D638
Supreme Petrochem SP 6456 High Heat Polystyrene Characteristics High heat resistance & strength Very good flow properties Available in any dark colorsProcessing Injection moldingApplications Instrument enclosures TV components Electrical encl..
Tensile Strength at Break	39.2 MPa	5690 psi	78% Ret.
UBE UBESTA® 3030U Nylon 12 (After Toluene for 1000 hours) Description: UBESTA has a strong resistance to chemicals. Under normal conditions, it is not significantly affected by alkalis, alcohols, ethers, ketones, hydrocarbons, lubricating oils, gasoline, c..
Tensile Strength at Break	39.2 MPa	5690 psi	50 mm/min; ASTM D638
Samsung Cheil Industries Infino® WP-1041G PC/ABS, Unreinforced Metal Plating Grade Information provided by Samsung Cheil Industries.