Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 53.9 MPa @Thickness 3.20 mm |
7820 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical Lupox® LW5102F PBT+PC+GF10% Description: Injection Molding, PBT+PC+GF10%, Low Warpage, Flame RetardantApplication: IT/OA, E&E (Switch)CAS No. 9003-01-04, 68928-70-1, 65997-17-3, 24968-12-5, 103598-77-2 and 1309-64-4Information.. |
|||
Tensile Strength at Break | 53.9 MPa @Thickness 3.20 mm |
7820 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical Lupox® SG3250 PBT+PET+MF25% Injection Molding, PBT+PET+MF25%, Good SurfaceApplication: Automotive (Head Lamp Bezel)CAS No. 24968-12-5, 25038-59-9 and 14807-96-6Information provided by LG Chemical |
|||
Tensile Strength at Break | 53.9 MPa | 7820 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® HN-3104 PC, 10% Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 53.9 MPa | 7820 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® HN-3104 PC, 10% Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 53.9 MPa | 7820 psi | ASTM D638 |
Unitika elitel UE3690 Polyester, Pellet High Tg, PET adhesiveness, High heat resistance, BinderUNITIKA l resins are thermoplastic saturated copolymeric polyester resins. l resins are expanding their applications from products such as ad.. |