Mechanical Properties | Metric | English | Comments |
---|---|---|---|
K (wear) Factor | 18.1 - 403 x 10-8 mm³/N-M | 9.00 - 200 x 10-10 in³-min/ft-lb-hr | Average value: 60.1 x 10<sup>-8</sup> mm³/N-M Grade Count:12 |
Overview of materials for Acetal Homopolymer, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Unreinforced". Each property range of values reported is minimum and maximum values .. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Lubricated: 0.25 m/s, 6.9 MPa (75 fpm, 1000 psi); ASTM D3702 |
Solvay Specialty Polymers Torlon® 4301 Polyamide-imide (PAI)
(Unverified Data**) Torlon 4301 is a wear-resistant grade of polyamide-imide (PAI) resin. It has a good balance of mechanical properties and wear resistance. It offers high flexural and compressive strength with a low .. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | |
Greene Tweed Avalon® 16 PTFE, Glass, Molybdenum Filled Products made from Avalon® thermoplastics are constructed from proprietary high-performance reinforced PTFE material. Greene, Tweeds Avalon thermoplastics, available in grades ranging from virgin.. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
SABIC Innovative Plastics LNP LUBRICOMP FL004 PE LNP* Lubricomp* FL004 is a compound based on Polyethylene resin containing 20% PTFE. Added features of this material include: Internally Lubricated. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
SABIC Innovative Plastics LNP LUBRICOMP IFL36 PA6.12 LNP LUBRICOMP* IFL36 is a compound based on Nylon 6/12 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
SABIC Innovative Plastics LNP LUBRICOMP IFL36R PA6.12 (Europe-Africa-Middle East) Internally lubricated PA6.12, containing Glass Fiber and PTFE |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
SABIC Innovative Plastics LNP LUBRICOMP KA000M POM (Europe-Africa-Middle East) LNP* LUBRICOMP* KA000M is a compound based on Acetal Copolymer resin containg Aramide and Proprietary Lubricant. Added features include Internally Lubricated. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
SABIC Innovative Plastics LNP LUBRICOMP KP004 Acetal LNP LUBRICOMP* KP004 is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
SABIC Innovative Plastics LNP LUBRICOMP KP004 Acetal Copolymer (Europe-Africa-Middle East) LNP* Lubricomp* KP004 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
SABIC Innovative Plastics LNP LUBRICOMP KP004A Acetal Homopolymer LNP* LUBRICOMP* KP004A is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
SABIC Innovative Plastics LNP LUBRICOMP KP004A Acetal Homopolymer (Europe-Africa-Middle East) LNP* LUBRICOMP* KP004A is a compound based on Acetal Homopolymer containing PTFE / Silicone. Added features include: Inernally Lubricated |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
SABIC Innovative Plastics LNP LUBRICOMP KP004AH Acetal Homopolymer LNP* LUBRICOMP* KP004AH is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added features of this material include: Wear Resistant |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
SABIC Innovative Plastics LNP LUBRICOMP KP004AXC Acetal Homopolymer LNP LUBRICOMP* KP004AXC is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
SABIC Innovative Plastics LNP LUBRICOMP KP004AXP POM (Europe-Africa-Middle East) LNP* LUBRICOMP* KP004AXP is a compound based on Acetal Homopolymer containing PTFE, Silicone. Added features include Internally Lubricated. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
SABIC Innovative Plastics LNP Lubricomp KP004AXZ Acetal Homopoly LNP* Lubricomp* KP004AXZ is a compound based on Acetal Homopolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP.. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
SABIC Innovative Plastics LNP LUBRICOMP KP004AXZ ACETAL HOMOPOLYMER LNP* LUBRICOMP* KP004AXZ is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
SABIC Innovative Plastics LNP LUBRICOMP KP004L Acetal Copoly LNP* LUBRICOMP* KP004L is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added features of this material include: Wear Resistant, Low Extractible. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
SABIC Innovative Plastics LNP LUBRICOMP KP004L Acetal Copoly (Asia Pacific) LNP* Lubricomp* KP004L is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
SABIC Innovative Plastics LNP LUBRICOMP KP004XXP Acetal Copolymer LNP LUBRICOMP* KP004XXP is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D3702 Modified |
SABIC Innovative Plastics LNP LUBRICOMP LFL36E PEEK LNP* LUBRICOMP* LFL36E is a compound based on Polyetheretherketone containing 30% Glass Fiber, 15% PTFE. Added features of this material are: Wear Resistant, Easy Molding. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | |
Techmer ES Luriblend® PA6 TSX10 Nylon 6 Availability: North AmericaForms: PelletsAdditive: PTFE Lubricant (10%)Features: Lubricated and Good Wear ResistanceInformation provided by TP Composites, Inc. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | |
TriStar TriSteel PR Metal Backed PTFE Bearing System Ultraflon 602e enhanced PTFE (PR) lined metal backed bearing , high speed reciprocating, self lubricating, high temperature and high load applications. Liner is designed specifically for high freque.. |
|||
K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | |
TriStar TriSteel PT Metal Backed PTFE Bearing System Ultraflon 602 (PT) PTFE lined metal backed bearing system, low friction, high PV, high speed sleeve, flange and thrust bearings, zero lube required, high operating temperature. Ultraflon 602 PTFE Li.. |
|||
K (wear) Factor | 18.1 - 121 x 10-8 mm³/N-M | 9.00 - 60.0 x 10-10 in³-min/ft-lb-hr | Average value: 38.0 x 10<sup>-8</sup> mm³/N-M Grade Count:7 |
Overview of materials for Acetal Homopolymer, PTFE-Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, PTFE-Filled". Each property range of values reported is minimum and maximum values o.. |