Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 753 MPa @Strain 0.200 %, Thickness 1.45 mm |
109000 psi @Strain 0.200 %, Thickness 0.0571 in |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Tensile Strength, Yield | 751 MPa @Strain 0.200 %, Thickness 12.7 mm |
109000 psi @Strain 0.200 %, Thickness 0.500 in |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Tensile Strength, Yield | 752 MPa @Temperature -55.0 °C |
109000 psi @Temperature -67.0 °F |
90°, Dry |
Hexcel® HexPly® 8552 Epoxy Matrix, A280-5H Fiber Information provided by HexCel |
|||
Tensile Strength, Yield | 752 MPa @Temperature 199 °C |
109000 psi @Temperature 390 °F |
Round bar 1" diameter, 310 HB |
EDRO #2 Prehardened 4130 Holder Block EDRO #2™ is a vacuum-degassed Chromium-Molybdenum-alloyed steel which is supplied in the hardened and tempered condition. EDRO #2™ is characterized by excellent machinability, good resistance to i.. |
|||
Tensile Strength, Yield | 752 MPa @Temperature 199 °C |
109000 psi @Temperature 390 °F |
Round bar 1" diameter, 310 HB |
EDRO #3 Prehardened Mold Quality P20 Alloy Steel EDRO #3™ is a vacuum-degassed, ladle refined, Cr-Ni-Mo- alloyed steel which is supplied in the hardened and tempered condition. EDRO #3™ is manufactured to consistently high quality standards with.. |
|||
Tensile Strength, Yield | 753 MPa @Strain 0.200 % |
109000 psi @Strain 0.200 % |
50% Cold Worked |
AK Steel 439 ULTRA FORM® Stainless Steel AK Steel 439 ULTRA FORM™ was developed for applications requiring oxidation and corrosion resistance superior to Type 409 as well as superior formability to AK Steel 439 Stainless Steel. As a resul.. |