Polymer Property : Tensile Strength, Yield = 111000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	765 MPa @Temperature -55.0 °C	111000 psi @Temperature -67.0 °F	0°, Dry
Hexcel® HexPly® 8552 Epoxy Matrix, A193-PW Fiber Information provided by HexCel
Tensile Strength, Yield	765 MPa @Temperature 93.3 °C	111000 psi @Temperature 200 °F	90°, Dry
Hexcel® HexPly® 8552 Epoxy Matrix, A193-PW Fiber Information provided by HexCel
Tensile Strength, Yield	768 MPa @Strain 0.200 %	111000 psi @Strain 0.200 %	Typical for Plate, 1/4-Hard, Transverse, 0.1875"
AK Steel NITRONIC® 30 Austenitic Stainless Steel AK Steel NITRONIC 30 Stainless Steel offers significantly higher strength than Type 304 and potential for applications requiring good resistance to aqueous and atmospheric corrosion resistance combi..
Tensile Strength, Yield	765 MPa @Strain 0.200 %	111000 psi @Strain 0.200 %	Longitudinal
AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 1150-M AK Steel 15-5 PH® provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base metal and welds. Short-time, ..
Tensile Strength, Yield	765 MPa @Strain 0.200 %	111000 psi @Strain 0.200 %	Transverse
AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 1150-M AK Steel 15-5 PH® provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base metal and welds. Short-time, ..
Tensile Strength, Yield	763 MPa @Strain 0.200 %, Thickness 25.4 mm	111000 psi @Strain 0.200 %, Thickness 1.00 in	Welded then age-hardened
Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl..