Polymer Property : Tensile Strength, Yield = 135 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	135 MPa @Strain 1.00 %, Temperature 700 °C	19600 psi @Strain 1.00 %, Temperature 1290 °F	EN min.
Outokumpu 153MA™ High Temperature Austenitic Stainless Steel Variant of 1.4301 with increased silicon and nitrogen contents and microalloyed with rare earth metals (REM). This raises the max service temperature in dry air to 1000°C.Applications: Heat and cr..
Tensile Strength, Yield	135 MPa @Strain 1.00 %, Temperature 300 °C	19600 psi @Strain 1.00 %, Temperature 572 °F	EN min.; EN 10002-5
Outokumpu 4301 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll..
Tensile Strength, Yield	135 MPa @Strain 1.00 %, Temperature 400 °C	19600 psi @Strain 1.00 %, Temperature 752 °F	EN min.; EN 10002-5
Outokumpu 4401 Cr-Ni-Mo Austenitic Stainless Steel General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot r..
Tensile Strength, Yield	135 MPa @Strain 0.200 %, Temperature 400 °C	19600 psi @Strain 0.200 %, Temperature 752 °F	EN min.; EN 10002-5
Outokumpu 4406 Cr-Ni-Mo Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms..
Tensile Strength, Yield	135 MPa @Thickness 9.50 - 25.4 mm, Temperature 982 Â°C	19600 psi @Thickness 0.374 - 1.00 in, Temperature 1800 Â°F	0.2% offset
Haynes HastelloyÂ® S alloy, flat products Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..