Polymer Property : Tensile Strength, Yield = 150 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	150 MPa @Strain 0.200 %, Temperature 300 °C	21800 psi @Strain 0.200 %, Temperature 572 °F	EN min.; EN 10002-5
Outokumpu 153MA™ High Temperature Austenitic Stainless Steel Variant of 1.4301 with increased silicon and nitrogen contents and microalloyed with rare earth metals (REM). This raises the max service temperature in dry air to 1000°C.Applications: Heat and cr..
Tensile Strength, Yield	150 MPa @Strain 0.200 %, Temperature 500 °C	21800 psi @Strain 0.200 %, Temperature 932 °F	EN min.; EN 10002-5
Outokumpu 253MA® High Temperature Austenitic Stainless Steel Variant of 1.4828 with increased nitrogen content and has been microalloyed with rare earth metals (REM). The most suitable temperature range is 850-1100°C, because structural changes when used be..
Tensile Strength, Yield	150 MPa @Strain 0.200 %, Temperature 400 °C	21800 psi @Strain 0.200 %, Temperature 752 °F	EN min.; EN 10002-5
Outokumpu 4439 Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), and cold rolled strip/sheet forms.
Tensile Strength, Yield	150 MPa @Strain 0.200 %, Thickness 5.00 - 20.0 mm	21800 psi @Strain 0.200 %, Thickness 0.197 - 0.787 in	Typical Strength
Constellium PLAN 5083 Aluminum Rolled Plate Rolled plates in 5083 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 5083 PLAN is mainly used for low stressed mechanical components, manufactured by intensive m..
Tensile Strength, Yield	150 MPa @Strain 0.200 %, Thickness 4.00 - 20.0 mm	21800 psi @Strain 0.200 %, Thickness 0.157 - 0.787 in	Typical Strength
Constellium PLAN 5754 Aluminum Rolled Plate Rolled plates in 5754 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 5754 PLAN is mainly used for low stressed mechanical components, manufactured by intensive m..
Tensile Strength, Yield	150 MPa @Strain 0.200 %, Thickness 4.00 - 20.0 mm	21800 psi @Strain 0.200 %, Thickness 0.157 - 0.787 in	Typical Strength
Constellium PLAN OX 5754 Aluminum Rolled Plate Rolled plates in 5754 PLAN OX are optimized for minimum residual stress, improved dimensional tolerances and for decorative* anodizing. 5754 PLAN OX is mainly used for low stressed, anodized compone..
Tensile Strength, Yield	150 MPa @Temperature 650 °C	21800 psi @Temperature 1200 °F
Crucible Compaction Metals Rene Supersolvus Rene 95 Nickel Based Superalloy Supersolvus P/M Rene 95 is designed to provide even higher temperature creep resistance and stress rupture strength than subsolvus Rene 95. Chemistry is not modified. These properties are obtained..
Tensile Strength, Yield	150 MPa @Strain 0.200 %, Thickness 6.00 - 20.0 mm	21800 psi @Strain 0.200 %, Thickness 0.236 - 0.787 in	Typical Strength
Constellium ALPLAN® 5083 Rolled Precision Aluminum Plate, Milled Both Sides ALPLAN® 5083 precision plates exhibit good dimensional stability. Their low internal stresses reduces the effects of plate deformation during machining, thus saving on extra operations such as roug..