| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 205 MPa @Strain 0.200 %, Temperature 100 °C |
29700 psi @Strain 0.200 %, Temperature 212 °F |
EN min.; EN 10002-5 |
| Outokumpu 4311 Cr-Ni Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.. |
|||
| Tensile Strength, Yield | >= 205 MPa @Temperature 20.0 °C |
>= 29700 psi @Temperature 68.0 °F |
|
| PEAK Werkstoff DISPAL S250 Aluminum Alloy, AlSi20Fe5Ni2, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
| Tensile Strength, Yield | 204.8 MPa @Thickness 2.40 mm, Temperature 427 °C |
29700 psi @Thickness 0.0945 in, Temperature 801 °F |
0.2% offset |
| Haynes Hastelloy® C-276 alloy, solution heat treated flat products Hastelloy® C-276 alloy is a nickel-molybdenum-chromium wrought alloy that is a versatile corrosion-resistant alloy. C-276 alloy is an improved wrought version of alloy C in that it usually doesn'.. |
|||
| Tensile Strength, Yield | 205 MPa @Thickness 12.7 mm, Temperature 538 °C |
29700 psi @Thickness 0.500 in, Temperature 1000 °F |
0.2% offset |
| Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
| Tensile Strength, Yield | 205 MPa @Strain 0.200 %, Temperature 100 °C |
29700 psi @Strain 0.200 %, Temperature 212 °F |
EN min.; EN 10002-5 |
| Outokumpu 904L High Performance Austenitic Stainless Steel Applications: Process equipment in chemical industryBleaching equipment in the pulp and paper industryFlue-gas cleaningDesalinationSeawater handlingHeat exchangersAvailable in hot rolled plate (Quar.. |
|||
| Tensile Strength, Yield | 205 MPa @Strain 1.00 %, Temperature 200 °C |
29700 psi @Strain 1.00 %, Temperature 392 °F |
EN min.; EN 10002-5 |
| Outokumpu 904L High Performance Austenitic Stainless Steel Applications: Process equipment in chemical industryBleaching equipment in the pulp and paper industryFlue-gas cleaningDesalinationSeawater handlingHeat exchangersAvailable in hot rolled plate (Quar.. |
|||