Polymer Property : Tensile Strength, Yield = 336 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	336 MPa @Thickness 6.30 mm, Temperature 20.0 Â°C	48700 psi @Thickness 0.248 in, Temperature 68.0 Â°F	0.2% offset
Haynes HastelloyÂ® C-4 alloy, plate, heat treated at 1066Â°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Tensile Strength, Yield	336 MPa @Thickness 9.50 mm, Temperature 20.0 °C	48700 psi @Thickness 0.374 in, Temperature 68.0 °F	0.2% offset
Haynes Hastelloy® C-4 alloy, sheet, aged 100 hours at 899°C Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..
Tensile Strength, Yield	336 MPa @Diameter 12.7 mm, Temperature 260 °C	48700 psi @Diameter 0.500 in, Temperature 500 °F	0.2% Offset
Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is..