- Polymer Property : Tensile Strength, Yield = 34800 psi
Polymer Property : Tensile Strength, Yield = 34800 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 240 MPa @Strain 1.00 %, Temperature 100 °C |
34800 psi @Strain 1.00 %, Temperature 212 °F |
EN min.; EN 10002-5 |
| Outokumpu 4311 Cr-Ni Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.. |
|||
| Tensile Strength, Yield | 240 MPa @Strain 1.00 %, Temperature -196 °C |
34800 psi @Strain 1.00 %, Temperature -321 °F |
EN min.; EN 10002-5 |
| Outokumpu 4541 Cr-Ni Austenitic Stainless Steel Good corrosion resistance and weldable. Resistant to sensitization.Applications: Welded screensFurnace beltsCatalytic converter meshAvailable in hot rolled plate (Quarto), hot rolled strip/sheet (C.. |
|||
| Tensile Strength, Yield | 240 MPa @Strain 1.00 %, Temperature -80.0 °C |
34800 psi @Strain 1.00 %, Temperature -112 °F |
EN min.; EN 10002-5 |
| Outokumpu 4541 Cr-Ni Austenitic Stainless Steel Good corrosion resistance and weldable. Resistant to sensitization.Applications: Welded screensFurnace beltsCatalytic converter meshAvailable in hot rolled plate (Quarto), hot rolled strip/sheet (C.. |
|||
| Tensile Strength, Yield | 240 MPa @Strain 1.00 %, Temperature 400 °C |
34800 psi @Strain 1.00 %, Temperature 752 °F |
EN min.; EN 10002-5 |
| Outokumpu 4565 High Performance Austenitic Stainless Steel Applications: Process equipment in chemical industryBleaching equipment in the pulp and paper industryFlue-gas cleaningDesalinationSeawater handlingHeat exchangersAvailable in hot rolled plate (Quar.. |
|||
| Tensile Strength, Yield | >= 240 MPa @Temperature 20.0 °C |
>= 34800 psi @Temperature 68.0 °F |
|
| PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
| Tensile Strength, Yield | >= 240 MPa @Strain 1.00 % |
>= 34800 psi @Strain 1.00 % |
|
| Industeel CLC 18.10 L General Purpose 18Cr-10Ni Austenitic Stainless Steel Description: CLC 18-10L is a 18Cr-10Ni austenitic stainless steel. The grade contains small amount of ferrite (~ 3%) after solution annealing (1000-1100°C – 1832-2012°F) and water quenchi.. |
|||
| Tensile Strength, Yield | >= 240 MPa @Strain 0.200 %, Thickness 60.0 - 80.0 mm |
>= 34800 psi @Strain 0.200 %, Thickness 2.36 - 3.15 in |
Temper T451; Standard EN 485-2 |
| Constellium ALPLAN® 2017A High-Strength Rolled Precision Aluminum Plate, Milled Both Sides ALPLAN® 2017A precision plates combine a very good dimensional stability with a high level of mechanical strength and elongation. The outstanding flatness, the low roughness and high quality of the.. |
|||
| Tensile Strength, Yield | >= 240 MPa @Strain 0.200 %, Thickness 40.0 - 80.0 mm |
>= 34800 psi @Strain 0.200 %, Thickness 1.57 - 3.15 in |
Temper T651; Standard EN 485-2 |
| Constellium PLAN 6061 Aluminum Rolled Plate Rolled plates in 6061 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 6061 PLAN is mainly used for medium stressed mechanical components, manufactured by intensiv.. |
|||
| Tensile Strength, Yield | >= 240 MPa @Strain 0.200 %, Thickness 80.0 - 100 mm |
>= 34800 psi @Strain 0.200 %, Thickness 3.15 - 3.94 in |
Temper T651; Standard EN 485-2 |
| Constellium PLAN 6061 Aluminum Rolled Plate Rolled plates in 6061 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 6061 PLAN is mainly used for medium stressed mechanical components, manufactured by intensiv.. |
|||
| Tensile Strength, Yield | >= 240 MPa @Strain 0.200 %, Thickness 12.5 - 60.0 mm |
>= 34800 psi @Strain 0.200 %, Thickness 0.492 - 2.36 in |
Temper T651; Standard EN 485-2 |
| Constellium PLAN 6082 Aluminum Rolled Plate Rolled plates in 6082 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 6082 PLAN is mainly used for medium stressed mechanical components, manufactured by intensiv.. |
|||
| Tensile Strength, Yield | >= 240 MPa @Strain 0.200 %, Thickness 60.0 - 100 mm |
>= 34800 psi @Strain 0.200 %, Thickness 2.36 - 3.94 in |
Temper T651; Standard EN 485-2 |
| Constellium PLAN 6082 Aluminum Rolled Plate Rolled plates in 6082 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 6082 PLAN is mainly used for medium stressed mechanical components, manufactured by intensiv.. |
|||
| Tensile Strength, Yield | >= 240 MPa @Strain 0.200 %, Thickness 12.5 - 60.0 mm |
>= 34800 psi @Strain 0.200 %, Thickness 0.492 - 2.36 in |
Temper T651; Standard EN 485-2 |
| Constellium Planoxal® 60 Aluminum plate The advantage of Planoxal®-60 plates over other standard EN AW-6082 alloy products is their low level of internal stress. They are also suitable for technical anodizing. Planoxal®-60 is mainly use.. |
|||
| Tensile Strength, Yield | >= 240 MPa @Strain 0.200 %, Thickness 60.0 - 80.0 mm |
>= 34800 psi @Strain 0.200 %, Thickness 2.36 - 3.15 in |
Temper T651; Standard EN 485-2 |
| Constellium Planoxal® 60 Aluminum plate The advantage of Planoxal®-60 plates over other standard EN AW-6082 alloy products is their low level of internal stress. They are also suitable for technical anodizing. Planoxal®-60 is mainly use.. |
|||
| Tensile Strength, Yield | 240 MPa @Temperature 816 °C |
34800 psi @Temperature 1500 °F |
|
| Crucible Steel XM-19 Stainless Steel Crucible XM-19 Stainless is a nitrogen strengthened, low carbon, austenitic, stainless steel that provides good corrosion resistance in combination with high strength. The alloy has better corrosio.. |
|||
| Tensile Strength, Yield | >= 240 MPa @Strain 0.200 %, Thickness 7.90 - 12.5 mm |
>= 34800 psi @Strain 0.200 %, Thickness 0.311 - 0.492 in |
Temper T651; Standard EN 485-2 |
| Constellium ALPLAN® 6061 Rolled Precision Aluminum Plate, Milled Both Sides Precision plates in ALPLAN® 6061 are milled on both sides and have a very low level of residual stress, thus avoiding excessive deformation during machining. Thanks to its very good dimensional sta.. |
|||
| Tensile Strength, Yield | >= 240 MPa @Strain 0.200 %, Thickness 12.5 - 40.0 mm |
>= 34800 psi @Strain 0.200 %, Thickness 0.492 - 1.57 in |
Temper T651; Standard EN 485-2 |
| Constellium ALPLAN® 6061 Rolled Precision Aluminum Plate, Milled Both Sides Precision plates in ALPLAN® 6061 are milled on both sides and have a very low level of residual stress, thus avoiding excessive deformation during machining. Thanks to its very good dimensional sta.. |
|||
| Tensile Strength, Yield | >= 240 MPa @Strain 0.200 %, Thickness 40.0 - 80.0 mm |
>= 34800 psi @Strain 0.200 %, Thickness 1.57 - 3.15 in |
Temper T651; Standard EN 485-2 |
| Constellium ALPLAN® 6061 Rolled Precision Aluminum Plate, Milled Both Sides Precision plates in ALPLAN® 6061 are milled on both sides and have a very low level of residual stress, thus avoiding excessive deformation during machining. Thanks to its very good dimensional sta.. |
|||
| Tensile Strength, Yield | >= 240 MPa @Strain 0.200 %, Thickness 100 - 140 mm |
>= 34800 psi @Strain 0.200 %, Thickness 3.94 - 5.51 in |
Temper T651; Standard EN 485-2 |
| Constellium ALPLAN® 6082 Rolled Precision Aluminum Plate, Milled Both Sides Precision plates in ALPLAN® 6082 are milled on both sides and have a very low level of residual stress, thus avoiding excessive deformation during machining. Thanks to its very good dimensional sta.. |
|||
| Tensile Strength, Yield | 240 MPa @Temperature 300 °C |
34800 psi @Temperature 572 °F |
|
| ATI Allegheny Ludlum AL 4565™ Corrosion Resistant Stainless Steel Characteristics:Very high resistance to pitting and crevice corrosion Excellent general corrosion resistance in a variety of media Higher mechanical propertied then conventional stainless steels Go.. |
|||
| Tensile Strength, Yield | 240 MPa @Temperature -40.0 °C |
34800 psi @Temperature -40.0 °F |
ISO 527 |
| BASF Ultramid® A3HG6 HR BK 23591 30% Glass Filled PA66 (Dry) Description: 30% glass-fiber reinforced injection-molding grade with enhanced hydrolysis resistance, e.g., for applications in vehicle cooling systems.Information provided by BASF |
|||
| Tensile Strength, Yield | >= 240 MPa @Strain 1.00 % |
>= 34800 psi @Strain 1.00 % |
|
| Industeel CLC 18.9 L General Purpose 18Cr-9Ni Austenitic Stainless Steel Description: CLC 18-9L is a 18Cr-9Ni austenitic stainless steel. The grade contains small amount of ferrite (~ 3%) after solution annealing (1000-1100°C – 1832-2012°F) and water quenching. This k.. |
|||