Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 390 MPa @Strain 0.200 % |
56600 psi @Strain 0.200 % |
Outokumpu Typical,Cold Rolled Strip/Sheet; EN 10002-1 |
Outokumpu 4372 Cr-Ni Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, and rod forms. |
|||
Tensile Strength, Yield | 390 MPa @Strain 1.00 % |
56600 psi @Strain 1.00 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 |
Outokumpu 4429 Cr-Ni-Mo Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), cold rolled strip/sheet and rod forms. |
|||
Tensile Strength, Yield | >= 390 MPa @Strain 0.200 %, Thickness 160 - 180 mm |
>= 56600 psi @Strain 0.200 %, Thickness 6.30 - 7.09 in |
|
Constellium Fortal® Aluminum Alloy Fortal® plates are optimized to provide high mechanical strength, combined with good shape stability and excellent machinability. Typical applications include sheet forming tools, base plates for m.. |
|||
Tensile Strength, Yield | >= 390 MPa @Strain 0.200 % |
>= 56600 psi @Strain 0.200 % |
Minimum |
Aleris Hokotol Aluminum Alloy, 325 mm Thickness Sample treatment not specified for property data.Applications include molds for blow forming and injection molding for plastics; bolsters and force plates; high strength/low weight machine parts; an.. |
|||
Tensile Strength, Yield | 390 MPa @Strain 0.200 %, Thickness 12.7 mm |
56600 psi @Strain 0.200 %, Thickness 0.500 in |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |