Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 421 MPa @Temperature 21.1 °C |
61000 psi @Temperature 70.0 °F |
0° Direction, Wet; ASTM D638 |
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 285 Kevlar® Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle.. |
|||
Tensile Strength, Yield | 421 MPa @Temperature 82.2 °C |
61000 psi @Temperature 180 °F |
0° Direction, Dry; Vacuum/Oven Cured; ASTM D3039-95 |
Park Electrochemical Nelcote® E-765 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-765 is a tough 250°F cure prepreg system designed to replace 350°F cure systems in aircraft structural applications. FAA-approved Design Allowable Databases are available upon request... |
|||
Tensile Strength, Yield | 421 MPa @Temperature 23.9 °C |
61000 psi @Temperature 75.0 °F |
0° Direction, Wet (2 hour water boil); ASTM D638 Type 1 |
Park Electrochemical Nelcote® P-650R Polyester Prepreg, 7781 E-Glass Reinforced Nelcote® P-650R is a non-styrenated/low VOC polyester resin system that has been designed for optical clarity. P-650 exhibits good mechanical properties up to 250°F.Key Features and Benefits:Non-s.. |
|||
Tensile Strength, Yield | 421 MPa @Temperature 121 °C |
61000 psi @Temperature 250 °F |
0° Direction, Wet; ASTM D638 Type 1 |
Park Electrochemical Nelcote® P-670I Polyester Prepreg, 7781 E-Glass Reinforced Nelcote® P-670I is a versatile, non-styrenated/low VOC polyester resin. P670I is used in a wide variety of applications including radomes, tooling and aircraft structures.Key Features and Benefits:.. |
|||
Tensile Strength, Yield | 421 MPa @Temperature 204 °C |
61000 psi @Temperature 400 °F |
0° Direction, Dry; ASTM D638 |
Park Electrochemical Nelcote® V-376 Cyanate Ester Epoxy Prepregs, 581 Quartz Reinforced Nelcote® V-376 is a Cyanate Ester matrix providing excellent electrical and mechanical properties for harsh aircraft, shipboard, and undersea applications for Radomes, Antenna, and Reflectors. Simp.. |
|||
Tensile Strength, Yield | 421 MPa @Thickness 3.17 mm, Temperature 20.0 °C |
61100 psi @Thickness 0.125 in, Temperature 68.0 °F |
0.2% offset |
Haynes Hastelloy® C-22® alloy, transverse, GTAW weldment, sheet - plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
Tensile Strength, Yield | 421 MPa @Strain 0.200 % |
61100 psi @Strain 0.200 % |
Longitudinal Orientation, True Stress/True Strain |
AK Steel 13-4 SR® Ferritic Stainless Steel AK Steel 13-4 SR Stainless Steel is a ductile weldable ferritic with 13% Cr and 3.75% Al. The high aluminum content results in a base alloy with high electrical resistivity. It is intended for use w.. |
|||
Tensile Strength, Yield | 421 MPa @Thickness 3.20 mm, Temperature 20.0 °C |
61100 psi @Thickness 0.126 in, Temperature 68.0 °F |
0.2% offset |
Haynes Hastelloy® C-4 alloy, sheet, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |