Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 51.7 - 75.8 MPa | 7500 - 11000 psi | ASTM D882 |
Honeywell ACLAR® 22A (2.00 mil) Copolymer Film
(discontinued **) Description: ACLAR® 22A is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It is a flexible transparent film used to package moisture sensitive products.Information provide.. |
|||
Film Tensile Strength at Break, MD | 51.7 - 75.8 MPa | 7500 - 11000 psi | ASTM D882 |
Honeywell ACLAR® 22A (1.50 mil) Copolymer Film
(discontinued **) Description: ACLAR® 22A is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It is a flexible transparent film used to package moisture sensitive products.Information provide.. |
|||
Film Tensile Strength at Break, MD | 30.0 - 75.8 MPa | 4350 - 11000 psi | Average value: 52.1 MPa Grade Count:28 |
Overview of materials for Linear Low Density Polyethylene (LLDPE), Blow Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "Linear Low Density Polyethylene (LLDPE), Blow Molding Grade". Each property range of values reported is .. |
|||
Film Tensile Strength at Break, MD | 55.4 - 75.8 MPa | 8040 - 11000 psi | Average value: 62.6 MPa Grade Count:9 |
Overview of materials for Thermoplastic Olefinic Elastomer (TPO), Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Olefinic Elastomer (TPO), Film Grade". Each property range of values reported is minimum a.. |