Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | ASTM-D882 |
Kinlead PL11 Lamination Grade BOPP Plain Film (thickness: 12 µm) PL11 is a general, lamination grade BOPP plain film. It is transparent and non heat sealable. It is excellent for extrusion lamination. One side has corona treatment. It is widely used in laminating.. |
|||
Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | ASTM-D882 |
Kinlead PL11 Lamination Grade BOPP Plain Film (thickness: 15 µm) PL11 is a general, lamination grade BOPP plain film. It is transparent and non heat sealable. It is excellent for extrusion lamination. One side has corona treatment. It is widely used in laminating.. |
|||
Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | ASTM-D882 |
Kinlead PL21 Lamination Grade BOPP Plain Film (thickness: 12 µm) PL21 is a general, lamination grade BOPP plain film. It is transparent and non heat sealable. It is excellent for extrusion lamination. It has excellent dimensional stability, high tensile strength,.. |
|||
Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | ASTM-D882 |
Kinlead PL21 Lamination Grade BOPP Plain Film (thickness: 15 µm) PL21 is a general, lamination grade BOPP plain film. It is transparent and non heat sealable. It is excellent for extrusion lamination. It has excellent dimensional stability, high tensile strength,.. |
|||
Film Tensile Strength at Break, MD | 150 - 180 MPa | 21800 - 26100 psi | ISO 527-3 |
Borealis BorPURE™ RB501BF Polypropylene Copolymer BorPure™ RB501BF is a random copolymer. Applications: BorPure™ RB501BF has been developed especially for applications like: food packaging, over wrap film, label film, and shrink film. Additives.. |
|||
Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor™ 18MB090 OPP Film Product Description: Biaxially oriented polypropylene film metallizable on one side, with a slip controlled broad seal range surface on the other side. Once metalized, film designed to be used in la.. |
|||
Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor™ 20MB080 OPP Film Product Description: Bicor 20NB080 is a biaxially oriented polypropylene film metallizable on one side, with a heat sealable surface on the other side. Designed to be used after metallization as a s.. |
|||
Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor™ 29MB080 OPP Film Product Description: A biaxially oriented polypropylene film metallizable on one side, with a heat sealable surface on the other side. Designed to be used after metallization as a single web in HFFS.. |
|||
Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Label-Lyte™ 29LL210 Preliminary Data Sheet OPP Film Product Description: A biaxially oriented, transparent polypropylene film for pressure sensitive labeling and tape applications.Availability: Africa & Middle East and EuropeKey Features: High yieldG.. |
|||
Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Metallyte™ 18MM383 OPP Film Product Description: A biaxially oriented very high barrier metalized polypropylene film. This film offers an outstanding moisture barrier and a broad seal range surface on the other side. This film.. |
|||
Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Metallyte™ 18MM388 OPP Film Product Description: A metallized biaxially oriented polypropylene film, metalized on one side with a broad seal range surface on the other side. This film is designed for high barrier performance p.. |
|||
Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Metallyte™ 18MM488 OPP Film Product Description: A metalized biaxially oriented polypropylene film, metalized on one side. MM488 is typically used in laminates as the inner web for VFFS and HFFS applications. Due to its slip c.. |
|||
Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Metallyte™ 18MM883 OPP Film Product Description: An ultra high barrier (UHB), biaxially oriented multilayer polypropylene film. This film has an exceptional barrier to oxygen, flavors and aromas and has an excellent water vapo.. |
|||
Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Metallyte™ 20MM480 OPP Film Product Description: A metalized biaxially oriented polypropylene film, metalized on one side, heat sealable on the other side. It is typically used in lamination with other substrates on HFFS and V.. |