Polymer Property : Film Tensile Strength at Break, MD = 18.6 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	18.6 MPa	2700 psi	Blown; ASTM D822
LyondellBasell PetrotheneÂ® NA373244 Low Density Polyethylene, Cast/Blown Film Grade ApplicationsPetrothene NA373 is a series of homopolymer resins selected by customers for use in household film and other applications that require high clarity and good impact strength combined with..
Film Tensile Strength at Break, MD	18.6 MPa	2700 psi	ASTM D882
LG Chemical LUTENE FB3000 LDPE Extrusion of Blown Film Description: LUTENE FB3000 is mainly intended for the extrusion of blown film with high mechanical property for the clarity bags in all thickness. LUTENE FB3000 have high mechanical property and ena..
Film Tensile Strength at Break, MD	18.6 MPa	2700 psi	Blown; ASTM D822
LyondellBasell PetrotheneÂ® NA373242 Low Density Polyethylene, Cast/Blown Film Grade ApplicationsPetrothene NA373 is a series of homopolymer resins selected by customers for use in household film and other applications that require high clarity and good impact strength combined with..
Film Tensile Strength at Break, MD	18.6 MPa	2700 psi	ASTM D882
Dow INTEGRAL™ 933 Tough Film for Lamination to Porous Substrates INTEGRAL 933 Adhesive Film has a low melting, high flow adhesive layer that is useful for bonding to substrates such as polyurethane or polyethylene foam, or to non-woven textiles.Information provid..
Film Tensile Strength at Break, MD	18.6 - 29.1 MPa	2700 - 4220 psi	Average value: 24.0 MPa Grade Count:3
Overview of materials for Low Density Polyethylene (LDPE), Blow Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Blow Molding Grade". Each property range of values reported is minimum ..